| 其它 其它 挤出 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃ | ASTM D-570 | Dry｜8.0 | % | |
| 吸水率 | 23℃ | ASTM D-570 | 3.0%Water｜- | % | |
| 吸水率 | 23℃，24hr | ASTM D-570 | Dry｜1.7 | % | |
| 吸水率 | 23℃，24hr | ASTM D-570 | 3.0%Water｜- | % | |
| 比重 | ASTM D-792 | Dry｜1.09 | |||
| 比重 | ASTM D-792 | 3.0%Water｜- | |||
| 拉伸屈服强度 | -40℃ | ASTM D-638 | Dry｜105 | MPa | |
| 拉伸屈服强度 | -40℃ | ASTM D-638 | 3.0%Water｜95 | MPa | |
| 洛氏硬度 | 23℃ | ASTM D-785 | Dry｜114 | R Scale | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 3.0%Water｜- | R Scale | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | Dry｜205 | J/m | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 3.0%Water｜690 | J/m | |
| IZOD缺口冲击强度 | -40℃ | ASTM D-256 | Dry｜175 | J/m | |
| IZOD缺口冲击强度 | -40℃ | ASTM D-256 | 3.0%Water｜- | J/m | |
| 断裂伸长率 | 23℃ | ASTM D-638 | Dry｜<200 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | Dry｜<200 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 3.0%Water｜<200 | % | |
| 弯曲模量 | -40℃ | ASTM D-790 | Dry｜2.9 | GPa | |
| 弯曲模量 | -40℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| 弯曲模量 | 23℃ | ASTM D-790 | Dry｜2.1 | GPa | |
| 弯曲模量 | 23℃ | ASTM D-790 | 3.0%Water｜0.7 | GPa | |
| 弯曲模量 | 80℃ | ASTM D-790 | Dry｜0.5 | GPa | |
| 弯曲模量 | 80℃ | ASTM D-790 | 3.0%Water｜- | GPa | |
| IZOD无缺口冲击强度 | 23℃ | ASTM D-256 | Dry｜不断裂 | KJ/m2 | |
| IZOD无缺口冲击强度 | 23℃ | ASTM D-256 | 3.0%Water｜- | KJ/m2 | |
| 断裂伸长率 | -40℃ | ASTM D-638 | Dry｜15 | % | |
| 断裂伸长率 | -40℃ | ASTM D-638 | 3.0%Water｜5.0 | % | |
| 拉伸屈服强度 | 80℃ | ASTM D-638 | Dry｜25 | MPa | |
| 拉伸屈服强度 | 80℃ | ASTM D-638 | 3.0%Water｜20 | MPa | |
| 拉伸屈服强度 | 23℃ | ASTM D-638 | Dry｜60 | MPa | |
| 拉伸屈服强度 | 23℃ | ASTM D-638 | 3.0%Water｜35 | MPa | |
| 弯曲强度 | -40℃ | ASTM D-790 | Dry｜130 | MPa | |
| 弯曲强度 | -40℃ | ASTM D-790 | 3.0%Water｜- | MPa | |
| 弯曲强度 | 23℃ | ASTM D-790 | Dry｜80 | MPa | |
| 弯曲强度 | 23℃ | ASTM D-790 | 3.0%Water｜- | MPa | |
| 熔点 | DSC | Dry｜225 | ℃ | ||
| 熔点 | DSC | 3.0%Water｜- | ℃ | ||
| 热变形温度 | 1.86MPa | ASTM D-648 | Dry｜67 | ℃ | |
| 热变形温度 | 1.86MPa | ASTM D-648 | 3.0%Water｜- | ℃ | |
| 热变形温度 | 0.46MPa | ASTM D-648 | Dry｜160 | ℃ | |
| 热变形温度 | 0.46MPa | ASTM D-648 | 3.0%Water｜- | ℃ | |
| 线性膨胀系数 | ASTM D-696 | Dry｜8-9 | 10-5/℃ | ||
| 线性膨胀系数 | ASTM D-696 | 3.0%Water｜- | 10-5/℃ | ||
| 关于日本东丽 CM1056价格 | |||||
| 1.有关“PA6 日本东丽 CM1056”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-15246-0.htmlPA6 日本东丽 CM1056
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。
下一篇：PA6 日本东丽 UTN141