| 玻纤增强 其它 其它 | |
| 特性：玻璃15%强化，一般用途。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜1.3 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 3%水｜- | % | |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 无水｜10 | mg/1000次 | |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 3%水｜- | mg/1000次 | |
| 比重 | ASTM D-792 | 无水｜1.25 | |||
| 比重 | ASTM D-792 | 3%水｜- | |||
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 无水｜6 | kg.cm/cm | |
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 3%水｜28 | kg.cm/cm | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜4 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 3%水｜<200 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 无水｜10 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 3%水｜<200 | % | |
| 断裂伸长率 | -40℃ | ASTM D-638 | 无水｜3.5 | % | |
| 断裂伸长率 | -40℃ | ASTM D-638 | 3%水｜<200 | % | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1700 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 3%水｜650 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜850 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 3%水｜400 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜2100 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 3%水｜1300 | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜- | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 3%水｜770 | Kg/cm2 | |
| 抗剪强度 | 80℃ | ASTM D-792 | 无水｜- | Kg/cm2 | |
| 抗剪强度 | 80℃ | ASTM D-792 | 3%水｜770 | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜119 | R-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 3%水｜100 | R-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜90 | M-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 3%水｜100 | M-标度 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜1200 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 3%水｜5300 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜550 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 3%水｜400 | Kg/cm2 | |
| 抗拉屈服强度 | -40 | ASTM D-638 | 无水｜1550 | Kg/cm2 | |
| 抗拉屈服强度 | -40 | ASTM D-638 | 3%水｜1100 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜51000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 3%水｜14000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜21000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 3%水｜5000 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜68000 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 3%水｜42000 | Kg/cm2 | |
| 体积电阻率 | ASTM D-257 | 无水｜1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 3%水｜1012-1013 | Ω.cm | ||
| 介电强度 | 1/8 | ASTM D-149 | 无水｜20 | KV/mm | |
| 介电强度 | 1/8 | ASTM D-149 | 3%水｜- | KV/mm | |
| 线性热膨胀系数 | ASTM D-696 | 无水｜4.5 | 10-5cm/cm.℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 3%水｜- | |||
| 比热 | 无水｜0.37 | Cal/g.°C | |||
| 比热 | 3%水｜- | Cal/g.°C | |||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜175 | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 3%水｜- | ℃ | |
| 熔点 | 差示扫描测热计DSC法 | 无水｜225 | ℃ | ||
| 熔点 | 差示扫描测热计DSC法 | 3%水｜- | ℃ | ||
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜210 | ℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 3%水｜- | ℃ | |
| 强化含量 | 无水｜15 | WT% | |||
| 强化含量 | 3%水｜- | WT% | |||
| 关于日本东丽 CM1011G-15价格 | |||||
| 1.有关“PA6 日本东丽 CM1011G-15”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-15256-0.htmlPA6 日本东丽 CM1011G-15