| 其它 其它 注塑 | |
| 特性：玻纤增强20%，高流动 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 24小时 23℃ | ASTM D-570 | 1.3 | % | |
| 比重 | ASTM D-792 | 1.29 | |||
| 泰伯磨耗量 | (1000g,CS-17)23 ℃ | ASTM D-1044 | 12 | mg/1000次 | |
| 强化含量 | 20 | WT% | |||
| 挠曲模量 | 23℃ | ASTM D-790 | 60000 | kg/cm | |
| 埃佐德衡击 | 23℃ V-缺口1/2 | ASTM D-256 | 6 | kgcm/cm | |
| 挠曲强度 | -40℃ | ASTM D-790 | 2400 | kg/cm | |
| 洛氏硬度 | R-标度 23℃ | ASTM D-785 | 120 | ||
| 裂断伸长率 | 23℃ | ASTM D-638 | 5 | % | |
| 挠曲模量 | -40℃ | ASTM D-790 | 78000 | kg/cm | |
| 洛氏硬度 | M-标度 23℃ | ASTM D-785 | 92 | ||
| 抗拉屈股强度 | 23℃ | ASTM D-638 | 1200 | kg/cm | |
| 挠曲模量 | 80℃ | ASTM D-790 | 29000 | kg/cm | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1800 | kg/cm | |
| 挠曲强度 | 80℃ | ASTM D-790 | 1000 | kg/cm | |
| 介电强度 | 1/8 短时间 | ASTM D-149 | 20 | KV/mm | |
| 体积电阻率 | ASTM D-257 | 10 | Ωcm | ||
| 熔点 | 差示扫描测热计DSC | 225 | ℃ | ||
| 热挠曲温度 | 18.6kg/cm | ASTM D-648 | 185 | ℃ | |
| 比热 | 0.36 | Cal/g℃ | |||
| 线性热膨胀系数 | ASTM D-696 | 3 | ×10 | ||
| 热挠曲温度 | 4.6kg/cm | ASTM D-648 | 215 | ℃ | |
| 关于日本东丽 CM1001G-20价格 | |||||
| 1.有关“PA6 日本东丽 CM1001G-20”物性表及PA6塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料的需求请与我们联系. | |||||