| 其它 其它 注塑 | |
| 试片状态调节：温度23±2℃；相对温度（R.H）50±50%；时间≥40hrs | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 黏度变异率 | QW-33QM-03 | 0.3 | |||
| 黏度 | QW-33CT-05 | X=2.7 | |||
| 降伏点抗拉强度 | ASTM D-638 | 755 | Kg/cm | ||
| 冲击强度 | -20℃ | ASTM D-256 | 2.6 | Kg.cm/cm | |
| 抗折弹性系数 | ASTM D-790 | 19050 | Kg/cm | ||
| 抗折强度 | ASTM D-790 | 915 | Kg/cm | ||
| 断裂点伸长率 | ASTM D-638 | 120 | % | ||
| 冲击强度 | 23℃ | ASTM D-256 | 7.5 | Kg.cm/cm | |
| 冲击强度 | -40℃ | ASTM D-256 | 3.0 | Kg.cm/cm | |
| 热变形温度 | 18.6Kgf/cm | ASTM D-648 | 82 | ℃ | |
| 热变形温度 | 4.6Kgf/cm | ASTM D-648 | 176 | ℃ | |
| 融点 | ASTM D-3418 | 217~224 | ℃ | ||
| 融点指数 | ASTM D-1238 | 22.0 | g/10mim | ||
| 相对密度 | ASTM D-1238 | 0.70 | Kg/cm | ||
| 水分 | QW-33CT-07 | 0.07 | % | ||
| 料筒温度 | 250~265 | ℃ | |||
| 灰分 | ASTM D-5630 | 0.01 | % | ||
| 相对密度 | ASTM D-1238 | 701 | g/cm | ||
| 洛氏硬度 | ASTM D-785 | 114 | |||
| 成型收缩率横向 | ASTM D-955 | 1.6 | % | ||
| 干燥条件 | 95//4 | ℃/hours | |||
| 成型收缩率纵向 | ASTM D-955 | 1.62 | % | ||
| 比重 | ASTM D-792 | 1.12 | g/cm | ||
| 关于台湾华隆 NC277价格 | |||||
| 1.有关“PA6 台湾华隆 NC277”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||