| 其它 其它 注塑 | |
| 紧固件，夹子，漆包线漆膜，单纤维 | |
| 低粘度，高流动性 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | 23℃ | ASTM D792 | 1.13 | ||
| 吸水性 | ASTM D570 | 1.7 | % | ||
| 模压收缩率 | 23℃ | ASTM D955 | 1.0-1.4 | % | |
| 洛氏硬度 | 120 | R-Scale | |||
| 抗张强度 | 50mm/min | ASTM D638 | 810 | kg/cm | |
| 抗张强度 | 50mm/min | ASTM D638 | 79.9 | MPa | |
| 抗张强度 | 50mm/min | ASTM D638 | 11518.2 | psi | |
| 休息时延长 | 50mm/min | ASTM D638 | 100 | % | |
| 弯曲强度 | 2.8mm/min | ASTM D790 | 1100 | kg/cm | |
| 弯曲强度 | 2.8mm/min | ASTM D790 | 108.6 | MPa | |
| 弯曲强度 | 2.8mm/min | ASTM D790 | 15642 | psi | |
| 弯曲模量 | 2.8mm/min | ASTM D790 | 27000 | kg/cm | |
| 弯曲模量 | 2.8mm/min | ASTM D790 | 2664.9 | MPa | |
| 弯曲模量 | 2.8mm/min | ASTM D790 | 383940 | psi | |
| IZOD冲击强度 | 23℃ | ASTM D256 | 5 | kg.cm/cm | |
| IZOD冲击强度 | 23℃ | ASTM D256 | 49 | J/m | |
| IZOD冲击强度 | 23℃ | ASTM D256 | 0.9 | ft.lb/in | |
| 电介质强度 | 23℃ | ASTM D149 | 19 | KV/mm | |
| 电容率 | 23℃ | ASTM D150 | 2.8 | ||
| 电孤阻 | 23℃ | ASTM D495 | 195 | sec | |
| 直流体积电阻率 | 23℃ | ASTM D257 | 10 | Ω.cm | |
| 熔点 | ASTM D789 | 220 | ℃ | ||
| 热变形温度 | 18.5kg/cm | ASTM D648 | 60 | ℃ | |
| 热变形温度 | 18.5kg/cm | ASTM D648 | 140 | ||
| 热变形温度 | 4.6kg/cm | ASTM D648 | 170 | ℃ | |
| 热变形温度 | 4.6kg/cm | ASTM D648 | 338 | ||
| 线性热膨胀系数 | ASTM D696 | 8 | |||
| 可燃性 | UL94 | V-2 | class | ||
| 关于LG化学 LG-1100A价格 | |||||
| 1.有关“PA6 LG化学 LG-1100A”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-15430-0.htmlPA6 LG化学 LG-1100A
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。
上一篇：PA6 泰国宇部 1015B
下一篇：PA6 德国巴斯夫 SEG7