| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.15到1.17 | g/cm3 | ||
| 吸水率 | 24hr | ASTMD570 | 0.50到0.60 | % | |
| 吸水率 | 饱和 | ASTMD570 | 5.0到6.0 | % | |
| 洛氏硬度(R级) | ASTMD785 | 115到125 | |||
| 肖氏硬度(邵氏D) | ASTMD2240 | 78到83 | |||
| 拉伸模量 | ASTMD638 | 2760到3790 | MPa | ||
| 抗张强度 | ASTMD638 | 68.9到93.1 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 20到55 | % | ||
| 弯曲模量 | ASTMD790 | 2900到3450 | MPa | ||
| 弯曲强度 | ASTMD790 | 107到121 | MPa | ||
| 压缩模量 | ASTMD695 | 2240到2760 | MPa | ||
| 压缩强度 | ASTMD695 | 93.1到110 | MPa | ||
| 剪切强度 | ASTMD732 | 68.9到75.8 | MPa | ||
| 摩擦系数(与自身-动态) | ASTMD1894 | 0.22 | |||
| 负载变形 | ASTMD621 | 0.500到2.50 | % | ||
| 悬壁梁缺口冲击强度 | ASTMD256 | 37到48 | J/m | ||
| 载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648 | 204到221 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648 | 93.3到204 | °C | |
| 连续使用温度 | ASTMD794 | 110 | °C | ||
| 熔融温度 | 227到238 | °C | |||
| 线形热膨胀系数-流动 | ASTMD696 | 1.1E-4 | cm/cm/°C | ||
| ServiceTemperature-Intermittent | 166 | °C | |||
| 介电强度 | ASTMD149 | 20到24 | kV/mm | ||
| 介电常数 | 60Hz | ASTMD150 | 3.70 | ||
| 介电常数 | 1kHz | ASTMD150 | 3.70 | ||
| 介电常数 | 100kHz | ASTMD150 | 3.70 | ||
| UL阻燃等级 | UL94 | HB | |||
| 关于美国Cast Nylons Nycast 6PA价格 | |||||
| 1.有关“PA6 美国Cast Nylons Nycast 6PA”物性表及PA6塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-41-20049-0.htmlPA6 美国Cast Nylons Nycast 6PA
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。