| 高强度,高光 | |
| 气球应用,包装,双向拉伸薄膜 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 摩擦系数 | 与金属-动态 | ASTMD1894 | 0.18 | ||
| 摩擦系数 | 与自身-动态 | ASTMD1894 | 0.50 | ||
| 薄膜厚度-经测试 | 12 | um | |||
| 割线模量 | MD:12um | ASTMD882 | 3100 | MPa | |
| 割线模量 | TD:12um | ASTMD882 | 2760 | MPa | |
| 抗张强度 | MD:断裂,12um | ASTMD882 | 276 | MPa | |
| 抗张强度 | TD:断裂,12um | ASTMD882 | 310 | MPa | |
| 伸长率 | MD:断裂,12um | ASTMD882 | 100 | % | |
| 伸长率 | TD:断裂,12um | ASTMD882 | 70 | % | |
| 透氧率(23°C,12um) | ASTMD3985 | 0.028 | cm3mm/m2/atm/24hr | ||
| 水气透过率(12um,38°C,100%RH) | ASTMF1249 | 2.6 | gmm/m2/atm/24hr | ||
| 薄膜厚度-经测试 | 12 | um | |||
| 割线模量 | MD:12um | ASTMD882 | 3100 | MPa | |
| 割线模量 | TD:12um | ASTMD882 | 2760 | MPa | |
| 抗张强度 | MD:断裂,12um | ASTMD882 | 276 | MPa | |
| 抗张强度 | TD:断裂,12um | ASTMD882 | 310 | MPa | |
| 伸长率 | MD:断裂,12um | ASTMD882 | 100 | % | |
| 伸长率 | TD:断裂,12um | ASTMD882 | 70 | % | |
| 透氧率(23°C,12um) | ASTMD3985 | 0.028 | cm3mm/m2/atm/24hr | ||
| 水气透过率(12um,38°C,100%RH) | ASTMF1249 | 2.6 | gmm/m2/atm/24hr | ||
| 关于美国Honeywell Capran Medallion® MT-1200价格 | |||||
| 1.有关“PA6 美国Honeywell Capran Medallion® MT-1200”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||