| 阻隔树脂,抗穿孔性,非触变性 | |
| 双向拉伸薄膜 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 摩擦系数 | 与金属-动态 | ASTMD1894 | 0.20 | ||
| 摩擦系数 | 与自身-动态 | ASTMD1894 | 0.50 | ||
| 薄膜厚度-经测试 | 14 | um | |||
| 割线模量 | MD:13um | ASTMD882 | 2550 | MPa | |
| 割线模量 | TD:13um | ASTMD882 | 2100 | MPa | |
| 抗张强度 | MD:断裂,13um | ASTMD882 | 272 | MPa | |
| 抗张强度 | TD:断裂,13um | ASTMD882 | 310 | MPa | |
| 伸长率 | MD:断裂,13um | ASTMD882 | 120 | % | |
| 伸长率 | TD:断裂,13um | ASTMD882 | 90 | % | |
| 透氧率 | 25°C,13um,0%RH | ASTMD3985 | 4.7 | cm3mm/m2/atm/24hr | |
| 透氧率 | 25°C,13um,65%RH | ASTMD3985 | 4.1 | cm3mm/m2/atm/24hr | |
| 水气透过率(14um,38°C,100%RH) | ASTMF1249 | 350 | gmm/m2/atm/24hr | ||
| 薄膜厚度-经测试 | 14 | um | |||
| 割线模量 | MD:13um | ASTMD882 | 2550 | MPa | |
| 割线模量 | TD:13um | ASTMD882 | 2100 | MPa | |
| 抗张强度 | MD:断裂,13um | ASTMD882 | 272 | MPa | |
| 抗张强度 | TD:断裂,13um | ASTMD882 | 310 | MPa | |
| 伸长率 | MD:断裂,13um | ASTMD882 | 120 | % | |
| 伸长率 | TD:断裂,13um | ASTMD882 | 90 | % | |
| 透氧率 | 25°C,13um,0%RH | ASTMD3985 | 4.7 | cm3mm/m2/atm/24hr | |
| 透氧率 | 25°C,13um,65%RH | ASTMD3985 | 4.1 | cm3mm/m2/atm/24hr | |
| 水气透过率(14um,38°C,100%RH) | ASTMF1249 | 350 | gmm/m2/atm/24hr | ||
| 光泽度(45°,13.5um) | ASTMD2457 | 108 | |||
| 雾度(13.5um) | ASTMD1003 | 2.0 | % | ||
| 关于美国Honeywell OxyShield® Plus 1350价格 | |||||
| 1.有关“PA6 美国Honeywell OxyShield® Plus 1350”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-20276-0.htmlPA6 美国Honeywell OxyShield® Plus 1350
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。