| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.07 | g/cm3 | ||
| 密度 | ISO1183 | 1.07 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 1.4 | % | |||
| 吸水率(24hr) | ASTMD570 | 1.1 | % | ||
| 吸水率(23°C,24hr) | ISO62 | 1.1 | % | ||
| 吸水率(饱和) | ASTMD570 | 6.7 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 6.7 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 1.9 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 1.9 | % | ||
| 拉伸模量 | -40°C | ISO527-2 | 2150 | MPa | |
| 拉伸模量 | 23°C | ISO527-2 | 1800 | MPa | |
| 拉伸模量 | 80°C | ISO527-2 | 210 | MPa | |
| 拉伸模量 | 120°C | ISO527-2 | 150 | MPa | |
| 拉伸模量 | 150°C | ISO527-2 | 130 | MPa | |
| 抗张强度 | 屈服,-40°C | ASTMD638 | 85.0 | MPa | |
| 抗张强度 | 屈服,23°C | ASTMD638 | 53.0 | MPa | |
| 抗张强度 | 屈服,80°C | ASTMD638 | 20.0 | MPa | |
| 抗张强度 | Yield,121°C | ASTMD638 | 14.0 | MPa | |
| 拉伸应力 | 屈服,-40°C | ISO527-2 | 85.0 | MPa | |
| 拉伸应力 | 屈服,23°C | ISO527-2 | 53.0 | MPa | |
| 拉伸应力 | 屈服,80°C | ISO527-2 | 20.0 | MPa | |
| 拉伸应力 | 屈服,120°C | ISO527-2 | 14.0 | MPa | |
| 拉伸应力 | 屈服,150°C | ISO527-2 | 9.00 | MPa | |
| 伸长率 | 屈服,-40°C | ASTMD638 | 8.0 | % | |
| 伸长率 | 屈服,23°C | ASTMD638 | 5.0 | % | |
| 伸长率 | 屈服,80°C | ASTMD638 | 37 | % | |
| 伸长率 | Yield,121°C | ASTMD638 | 27 | % | |
| 拉伸应变(屈服,23°C) | ISO527-2 | 5.0 | % | ||
| 伸长率(断裂,23°C) | ASTMD638 | >100 | % | ||
| 标称拉伸断裂应变(23°C) | ISO527-2 | >50 | % | ||
| 弯曲模量 | -40°C | ASTMD790 | 2300 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 1800 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 270 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 210 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 165 | MPa | |
| 弯曲模量(23°C) | ISO178 | 1750 | MPa | ||
| 弯曲强度 | -40°C | ASTMD790 | 120 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 65.0 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 20.0 | MPa | |
| 弯曲强度 | 90°C | ASTMD790 | 10.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 10.0 | MPa | |
| 弯曲应力(23°C) | ISO178 | 50.0 | MPa | ||
| 简支梁缺口冲击强度 | -30°C | ISO179 | 15 | kJ/m2 | |
| 简支梁缺口冲击强度 | 23°C | ISO179 | 100 | kJ/m2 | |
| 简支梁无缺口冲击强度(23°C) | ISO179 | NoBreak | |||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 190 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | NoBreak | ||
| 洛氏硬度(R级) | ASTMD785 | 78 | |||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 145 | °C | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/B | 145 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 56.0 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 51.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 溶融温度（DSC） | ISO3146 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 1.1E-4 | cm/cm/°C | ||
| RTIElec | 1.5mm | UL746 | 65.0 | °C | |
| RTIElec | 3.0mm | UL746 | 65.0 | °C | |
| RTIImp | 1.5mm | UL746 | 65.0 | °C | |
| RTIImp | 3.0mm | UL746 | 65.0 | °C | |
| RTIStr | 1.5mm | UL746 | 65.0 | °C | |
| RTIStr | 3.0mm | UL746 | 65.0 | °C | |
| VolumeResistivity(1.50mm) | ASTMD257 | >1.0E+13 | ohmscm | ||
| 关于德国巴斯夫 Ultramid® 8350 HS价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8350 HS”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-20500-0.htmlPA6 德国巴斯夫 Ultramid® 8350 HS
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。