| 耐碳氢化合物,可切削 浇铸 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.15 | g/cm3 | ||
| 吸水率 | 24hr | ASTMD570 | 0.60 | % | |
| 吸水率 | 饱和 | ASTMD570 | 7.0 | % | |
| 洛氏硬度 | M级 | ASTMD785 | 85 | ||
| 洛氏硬度 | R级 | ASTMD785 | 115 | ||
| 肖氏硬度(邵氏D) | ASTMD2240 | 85 | |||
| 拉伸模量 | ASTMD638 | 2760 | MPa | ||
| 抗张强度(极限) | ASTMD638 | 82.7 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 20 | % | ||
| 弯曲模量 | ASTMD790 | 3450 | MPa | ||
| 弯曲强度(屈服) | ASTMD790 | 110 | MPa | ||
| 压缩模量 | ASTMD695 | 2760 | MPa | ||
| 压缩强度(10%应变) | ASTMD695 | 103 | MPa | ||
| 剪切强度 | ASTMD732 | 75.8 | MPa | ||
| 摩擦系数(与钢-静态) | 内部方法 | 0.20 | |||
| 磨损因数 | ASTMD3702 | 200 | 10^-8mm3/Nm | ||
| 悬壁梁缺口冲击强度 | ASTMD256A | 21 | J/m | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 93.3 | °C | ||
| 最高使用温度-LongTerm,Air | 93 | °C | |||
| 结晶峰温度(DSC) | ASTMD3418 | 216 | °C | ||
| 线形热膨胀系数-流动2(-40到149°C) | ASTME831 | 9.0E-5 | cm/cm/°C | ||
| 导热系数 | ASTMF433 | 0.25 | W/m/K | ||
| 表面电阻率3 | 内部方法 | >1.0E+13 | ohms | ||
| 介电强度4 | ASTMD149 | 20 | kV/mm | ||
| 介电常数(1MHz) | ASTMD150 | 3.70 | |||
| UL阻燃等级(3.2mm,EstimatedRating) | UL94 | HB | |||
| LimitingPressureVelocity5 | 内部方法 | 0.105 | MPam/s | ||
| 关于瑞士跨骏 Quadrant EPP Nylatron® MC® 907价格 | |||||
| 1.有关“PA6 瑞士跨骏 Quadrant EPP Nylatron® MC® 907”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-20637-0.htmlPA6 瑞士跨骏 Quadrant EPP Nylatron® MC® 907
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。