| 通用 注射成型 | |
| 外壳,电器用具,电气/电子应用领域 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.49 | g/cm3 | ||
| 收缩率-流动(3.20mm) | ASTMD955 | 0.40to0.80 | % | ||
| 吸水率(24hr) | ASTMD570 | 1.0 | % | ||
| TensileStrength2(Break,3.20mm) | ASTMD638 | 83.4 | MPa | ||
| 伸长率2(断裂,3.20mm) | ASTMD638 | 3.0 | % | ||
| 弯曲模量3(3.20mm) | ASTMD790 | 6860 | MPa | ||
| 弯曲强度4(屈服,3.20mm) | ASTMD790 | 127 | MPa | ||
| 悬壁梁缺口冲击强度(23°C,3.20mm) | ASTMD256 | 69 | J/m | ||
| 洛氏硬度(R级) | ASTMD785 | 121 | |||
| 载荷下热变形温度(0.45MPa,未退火,6.40mm) | ASTMD648 | 210 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | ASTMD648 | 180 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTMD696 | 5.1E-5 | cm/cm/°C | ||
| RTIElec | 1.5mm | UL746 | 120 | °C | |
| RTIElec | 3.0mm | UL746 | 120 | °C | |
| RTIImp | 1.5mm | UL746 | 105 | °C | |
| RTIImp | 3.0mm | UL746 | 105 | °C | |
| RTIStr | 1.5mm | UL746 | 120 | °C | |
| RTIStr | 3.0mm | UL746 | 120 | °C | |
| 体积电阻率 | ASTMD257 | 1.0E+17 | ohmscm | ||
| 介电强度(1.00mm) | ASTMD149 | 22 | kV/mm | ||
| 介电常数(1MHz) | ASTMD150 | 4.00 | |||
| 耐电弧性 | ASTMD495 | 185 | sec | ||
| UL阻燃等级 | 0.75mm | UL94 | HB | ||
| UL阻燃等级 | 1.5mm | UL94 | HB | ||
| UL阻燃等级 | 3.0mm | UL94 | HB | ||
| 关于韩国LG化学 Lumid® GP3400A(W)价格 | |||||
| 1.有关“PA6 韩国LG化学 Lumid® GP3400A(W)”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-20832-0.htmlPA6 韩国LG化学 Lumid® GP3400A(W)