| 中等抗撞击性 注射成型 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.11 | g/cm3 | ||
| 熔流率（熔体流动速率）(235°C/1.0kg) | ASTMD1238 | 5.0 | g/10min | ||
| 收缩率-流动 | ASTMD955 | 1.5to1.9 | % | ||
| 抗张强度 | ASTMD638 | 65.5 | MPa | ||
| 伸长率(屈服) | ASTMD638 | 5.0 | % | ||
| 伸长率(断裂) | ASTMD638 | 50 | % | ||
| 弯曲模量 | ASTMD790 | 2210 | MPa | ||
| 弯曲强度 | ASTMD790 | 82.7 | MPa | ||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 130 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 190 | J/m | |
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 60.0 | °C | ||
| 熔融温度 | DSC | 216 | °C | ||
| 线形热膨胀系数-流动 | ASTMD696 | 8.5E-5 | cm/cm/°C | ||
| RTIElec | 0.8mm | UL746 | 65.0 | °C | |
| RTIElec | 1.5mm | UL746 | 65.0 | °C | |
| RTIElec | 3.0mm | UL746 | 65.0 | °C | |
| RTIImp | 0.8mm | UL746 | 65.0 | °C | |
| RTIImp | 1.5mm | UL746 | 65.0 | °C | |
| RTIImp | 3.0mm | UL746 | 65.0 | °C | |
| RTIStr | 0.8mm | UL746 | 65.0 | °C | |
| RTIStr | 1.5mm | UL746 | 65.0 | °C | |
| RTIStr | 3.0mm | UL746 | 65.0 | °C | |
| 体积电阻率 | ASTMD257 | 1.0E+13 | ohmscm | ||
| 介电强度(3.00mm) | ASTMD149 | 12 | kV/mm | ||
| 相比耐漏电起痕指数(CTI) | UL746 | 600 | V | ||
| UL阻燃等级(0.8mm) | UL94 | HB | |||
| 极限氧指数 | ASTMD2863 | 21 | % | ||
| 关于Chem Polymer公司 Chemlon® 253价格 | |||||
| 1.有关“PA6 Chem Polymer公司 Chemlon® 253”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||