| 注射成型 | |
| 填料：玻璃纤维增强材料, 14% 填料按重量。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.23 | g/cm3 | ||
| 收缩率-流动 | ASTMD955 | 0.50to1.0 | % | ||
| 抗张强度 | ASTMD638 | 114 | MPa | ||
| 伸长率(屈服) | ASTMD638 | 3.0 | % | ||
| 伸长率(断裂) | ASTMD638 | 3.0 | % | ||
| 弯曲模量 | ASTMD790 | 4310 | MPa | ||
| 弯曲强度 | ASTMD790 | 162 | MPa | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 64 | J/m | ||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 204 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 188 | °C | ||
| 熔融温度 | DSC | 216 | °C | ||
| 线形热膨胀系数-流动 | ASTMD696 | 5.5E-5 | cm/cm/°C | ||
| RTIElec | 0.8mm | UL746 | 105 | °C | |
| RTIElec | 1.5mm | UL746 | 105 | °C | |
| RTIElec | 3.0mm | UL746 | 105 | °C | |
| RTIImp | 0.8mm | UL746 | 75.0 | °C | |
| RTIImp | 1.5mm | UL746 | 75.0 | °C | |
| RTIImp | 3.0mm | UL746 | 75.0 | °C | |
| RTIStr | 0.8mm | UL746 | 105 | °C | |
| RTIStr | 1.5mm | UL746 | 105 | °C | |
| RTIStr | 3.0mm | UL746 | 105 | °C | |
| 体积电阻率 | ASTMD257 | 1.0E+14 | ohmscm | ||
| 介电强度(3.00mm) | ASTMD149 | 11 | kV/mm | ||
| 相比耐漏电起痕指数(CTI) | UL746 | 500 | V | ||
| UL阻燃等级(0.8mm) | UL94 | HB | |||
| 极限氧指数 | ASTMD2863 | 22 | % | ||
| FMVSS可燃性 | FMVSS302 | PASSES | |||
| 关于Chem Polymer公司 Chemlon® 214 G价格 | |||||
| 1.有关“PA6 Chem Polymer公司 Chemlon® 214 G”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||