| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ISO1183 | 1.51 | g/cm3 | ||
| 拉伸模量2 | ASTMD638 | 8270 | MPa | ||
| 拉伸模量 | ISO527-2/1 | 7880 | MPa | ||
| 抗张强度(屈服) | ASTMD638 | 110 | MPa | ||
| 拉伸应力(屈服) | ISO527-2 | 113 | MPa | ||
| 抗张强度(断裂) | ASTMD638 | 110 | MPa | ||
| 拉伸应力(断裂) | ISO527-2 | 113 | MPa | ||
| 伸长率(屈服) | ASTMD638 | 5.8 | % | ||
| 拉伸应变(屈服) | ISO527-2 | 4.1 | % | ||
| 伸长率(断裂) | ASTMD638 | 6.7 | % | ||
| 拉伸应变(断裂) | ISO527-2 | 4.5 | % | ||
| 弯曲模量 | ASTMD790 | 5520 | MPa | ||
| 弯曲模量 | ISO178 | 7000 | MPa | ||
| 弯曲应力 | ISO178 | 172 | MPa | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 150 | J/m | ||
| 悬壁梁缺口冲击强度3(23°C) | ISO180/1A | 17 | kJ/m2 | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD4812 | 1100 | J/m | ||
| UnnotchedIzodImpactStrength3(23°C) | ISO180/1U | 79 | kJ/m2 | ||
| 装有测量仪表的落镖冲击(23°C,EnergyatPeakLoad) | ASTMD3763 | 19.0 | J | ||
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 216 | °C | ||
| HeatDeflectionTemperature4(0.45MPa,Unannealed,64.0mmSpan) | ISO75-2/Bf | 216 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 201 | °C | ||
| 热变形温度4(1.8MPa,未退火,64.0mm跨距) | ISO75-2/Af | 202 | °C | ||
| 关于沙伯基础 LNP™ LUBRICOMP™ PFL36 compound价格 | |||||
| 1.有关“PA6 沙伯基础 LNP™ LUBRICOMP™ PFL36 compound”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-21475-0.htmlPA6 沙伯基础 LNP™ LUBRICOMP™ PFL36 compound
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。