| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ISO1183,ASTMD792 | 1.61 | g/cm3 | ||
| 收缩率 | 流动:24小时 | ASTMD955 | 0.15 | % | |
| 收缩率 | 横向流动:24小时 | ASTMD955 | 0.17 | % | |
| ――1 | ASTMD638 | 10800 | MPa | ||
| ―― | ISO527-2/1 | 16000 | MPa | ||
| 断裂2 | ASTMD638 | 54.0 | MPa | ||
| 断裂 | ISO527-2/5 | 75.0 | MPa | ||
| 断裂3 | ASTMD638 | 1.0 | % | ||
| 断裂 | ISO527-2/5 | 0.90 | % | ||
| 50.0mm跨距4 | ASTMD790 | 12400 | MPa | ||
| ――5 | ISO178 | 14000 | MPa | ||
| ――6 | ISO178 | 90.0 | MPa | ||
| 断裂,50.0mm跨距7 | ASTMD790 | 78.0 | MPa | ||
| 23°C | ASTMD256 | 26 | J/m | ||
| 23°C8 | ISO180/1A | 3.0 | kJ/m2 | ||
| 23°C | ASTMD4812 | 150 | J/m | ||
| 23°C9 | ISO180/1U | 8.0 | kJ/m2 | ||
| 1.8MPa,未退火,3.20mm | ASTMD648 | 186 | °C | ||
| 1.8MPa,未退火,64.0mm跨距10 | ISO75-2/Af | 200 | °C | ||
| BallPressureTest(165°C) | IEC60695-10-2 | Pass | |||
| 流动:-40到40°C | ASTME831 | 1.6E-5 | cm/cm/°C | ||
| 流动:-30到80°C | ISO11359-2 | 1.4E-5 | cm/cm/°C | ||
| 流动:23到80°C | ISO11359-2 | 1.6E-5 | cm/cm/°C | ||
| 横向:-40到40°C | ASTME831 | 3.6E-5 | cm/cm/°C | ||
| 横向:-30到80°C | ISO11359-2 | 4.0E-5 | cm/cm/°C | ||
| 横向:23到80°C | ISO11359-2 | 4.8E-5 | cm/cm/°C | ||
| ――11 | ASTME1461 | 3.5 | W/m/K | ||
| ――12 | ASTME1461 | 15 | W/m/K | ||
| ――13 | ISO22007-2 | 1.5 | W/m/K | ||
| ――14 | ISO22007-2 | 18 | W/m/K | ||
| 表面电阻率 | ASTMD257 | 3.0E+5 | ohms | ||
| UL阻燃等级(1.00mm) | UL94 | HB | |||
| 灼热丝易燃指数 | 1.00mm | IEC60695-2-12 | 850650 | °C | |
| 灼热丝易燃指数 | 1.60mm | IEC60695-2-12 | 960 | °C | |
| 热灯丝点火温度(1.00mm) | IEC60695-2-13 | 825 | °C | ||
| 关于沙伯基础 LNP™ KONDUIT™ PX10323 compound价格 | |||||
| 1.有关“PA6 沙伯基础 LNP™ KONDUIT™ PX10323 compound”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-21747-0.htmlPA6 沙伯基础 LNP™ KONDUIT™ PX10323 compound
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。