| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.11 | g/cm3 | ||
| 吸水率 | 24hr | ASTMD570 | 0.47 | % | |
| 吸水率 | 饱和 | ASTMD570 | 7.0 | % | |
| 洛氏硬度(M级) | ASTMD785 | 65 | |||
| 拉伸模量 | ASTMD638 | 2760 | MPa | ||
| 抗张强度(极限) | ASTMD638 | 62.1 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 15 | % | ||
| 弯曲模量 | ASTMD790 | 2480 | MPa | ||
| 弯曲强度(屈服) | ASTMD790 | 89.6 | MPa | ||
| 压缩模量 | ASTMD695 | 2480 | MPa | ||
| 压缩强度(10%应变) | ASTMD695 | 68.9 | MPa | ||
| 摩擦系数(与钢-静态) | 内部方法 | 0.14 | |||
| 磨损因数 | ASTMD3702 | 52 | 10^-8mm3/Nm | ||
| 悬壁梁缺口冲击强度 | ASTMD256A | 37 | J/m | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 93.3 | °C | ||
| 最高使用温度-LongTerm,Air | 93 | °C | |||
| 结晶峰温度(DSC) | ASTMD3418 | 216 | °C | ||
| 线形热膨胀系数-流动2(-40到149°C) | ASTME831 | 8.8E-5 | cm/cm/°C | ||
| 表面电阻率3 | 内部方法 | >1.0E+12 | ohms | ||
| UL阻燃等级(3.2mm,EstimatedRating) | UL94 | HB | |||
| LimitingPressureVelocity4 | 内部方法 | 0.596 | MPam/s | ||
| 关于瑞士跨骏 Quadrant EPP Nylatron® 703 XL价格 | |||||
| 1.有关“PA6 瑞士跨骏 Quadrant EPP Nylatron® 703 XL”物性表及PA6塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料的需求请与我们联系. | |||||