| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ASTMD1505 | 1.12 | g/cm3 | ||
| 熔流率（熔体流动速率）(235°C/1.0kg) | ASTMD1238 | 23 | g/10min | ||
| 收缩率-流动 | ASTMD955 | 1.3 | % | ||
| 吸水率 | 24hr | ASTMD570 | 1.6 | % | |
| 吸水率 | 饱和 | ASTMD570 | 9.5 | % | |
| 吸水率 | 平衡,50%RH | ASTMD570 | 2.7 | % | |
| 含水量 | ASTMD6869 | <0.10 | % | ||
| 相对粘度 9ab7daa3ac>[email protected]%SAV | 2.34 | ||||
| 粘度-FAV | ASTMD789 | 33.0到39.0 | |||
| 洛氏硬度(R级) | ASTMD785 | 119 | |||
| 拉伸模量(23°C) | ASTMD638 | 2750 | MPa | ||
| 抗张强度(屈服,23°C) | ASTMD638 | 79.0 | MPa | ||
| 伸长率 | 屈服,23°C | ASTMD638 | 4.1 | % | |
| 伸长率 | 断裂,23°C | ASTMD638 | 75 | % | |
| 弯曲模量(23°C) | ASTMD790 | 2470 | MPa | ||
| 弯曲强度(23°C) | ASTMD790 | 96.0 | MPa | ||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 45 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 46 | J/m | |
| 载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648 | 152 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648 | 47.0 | °C | |
| 载荷下热变形温度 | 熔融温度 | ASTMD648 | 222 | °C | |
| 线形热膨胀系数-流动 | ASTME831 | 7.2E-5 | cm/cm/°C | ||
| 关于美国Honeywell Aegis® H35ZI价格 | |||||
| 1.有关“PA6 美国Honeywell Aegis® H35ZI”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-21935-0.htmlPA6 美国Honeywell Aegis® H35ZI
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。