| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 密度 | ISO1183 | 1.13 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 1.2 | % | |||
| 吸水率(24hr) | ASTMD570 | 1.6 | % | ||
| 吸水率(23°C,24hr) | ISO62 | 1.6 | % | ||
| 吸水率(饱和) | ASTMD570 | 9.5 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 9.5 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 2.7 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 2.7 | % | ||
| 拉伸模量(23°C) | ISO527-2 | 2700 | MPa | ||
| 抗张强度 | 屈服,-40°C | ASTMD638 | 136 | MPa | |
| 抗张强度 | 屈服,23°C | ASTMD638 | 85.0 | MPa | |
| 抗张强度 | Yield,121°C | ASTMD638 | 23.0 | MPa | |
| 拉伸应力 | 屈服,-40°C | ISO527-2 | 136 | MPa | |
| 拉伸应力 | 屈服,23°C | ISO527-2 | 80.0 | MPa | |
| 拉伸应力 | 屈服,120°C | ISO527-2 | 23.0 | MPa | |
| 伸长率 | 屈服,-40°C | ASTMD638 | 3.0 | % | |
| 伸长率 | 屈服,23°C | ASTMD638 | 20 | % | |
| 伸长率 | Yield,121°C | ASTMD638 | 15 | % | |
| 拉伸应变(屈服,23°C) | ISO527-2 | 5.0 | % | ||
| 伸长率 | 断裂,-40°C | ASTMD638 | 8.0 | % | |
| 伸长率 | 断裂,23°C | ASTMD638 | 60 | % | |
| 伸长率 | Break,121°C | ASTMD638 | >100 | % | |
| 标称拉伸断裂应变 | -40°C | ISO527-2 | 8.0 | % | |
| 标称拉伸断裂应变 | 23°C | ISO527-2 | 25 | % | |
| 标称拉伸断裂应变 | 120°C | ISO527-2 | >100 | % | |
| 弯曲模量 | -40°C | ASTMD790 | 3010 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 2830 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 460 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 350 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 305 | MPa | |
| 弯曲模量(23°C) | ISO178 | 2400 | MPa | ||
| 弯曲强度 | -40°C | ASTMD790 | 168 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 110 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 30.0 | MPa | |
| 弯曲强度 | 90°C | ASTMD790 | 20.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 18.0 | MPa | |
| 弯曲应力(23°C) | ISO178 | 82.0 | MPa | ||
| 简支梁缺口冲击强度(23°C) | ISO179 | 3.5 | kJ/m2 | ||
| 简支梁无缺口冲击强度(23°C) | ISO179 | NoBreak | |||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 48 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 65 | J/m | |
| 洛氏硬度(R级) | ASTMD785 | 119 | |||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 175 | °C | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/B | 150 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 65.0 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 60.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 溶融温度（DSC） | ISO3146 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 8.3E-5 | cm/cm/°C | ||
| RTIElec | 0.71mm | UL746 | 130 | °C | |
| RTIElec | 1.3mm | UL746 | 130 | °C | |
| RTIElec | 3.0mm | UL746 | 130 | °C | |
| RTIElec | 6.0mm | UL746 | 130 | °C | |
| RTIImp | 0.71mm | UL746 | 95.0 | °C | |
| RTIImp | 1.3mm | UL746 | 105 | °C | |
| RTIImp | 3.0mm | UL746 | 105 | °C | |
| RTIImp | 6.0mm | UL746 | 105 | °C | |
| RTIStr | 0.71mm | UL746 | 95.0 | °C | |
| RTIStr | 1.3mm | UL746 | 105 | °C | |
| RTIStr | 3.0mm | UL746 | 105 | °C | |
| RTIStr | 6.0mm | UL746 | 105 | °C | |
| UL阻燃等级 | 3.0mm | UL94 | V-2 | ||
| 关于德国巴斯夫 Ultramid® 8200 HS价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8200 HS”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||