| 成核的,通用,润滑 注射成型 | |
| 通用 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 收缩率-流动(3.18mm) | ASTMD955 | 0.80到1.2 | % | ||
| 抗张强度 | 屈服,3.18mm | ASTMD638 | 89.6 | MPa | |
| 抗张强度 | 断裂,3.18mm | ASTMD638 | 89.6 | MPa | |
| 弯曲模量(3.18mm) | ASTMD790 | 3100 | MPa | ||
| 弯曲强度(3.18mm) | ASTMD790 | 108 | MPa | ||
| 悬壁梁缺口冲击强度(23°C,3.18mm) | ASTMD256 | 53 | J/m | ||
| 落锤冲击(3.18mm) | ASTMD3029 | 36.2 | J | ||
| 载荷下热变形温度 | 0.45MPa,未退火,3.18mm | ASTMD648 | 191 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火,3.18mm | ASTMD648 | 73.9 | °C | |
| RTIElec | 0.8mm | UL746 | 125 | °C | |
| RTIElec | 1.5mm | UL746 | 125 | °C | |
| RTIElec | 3.0mm | UL746 | 125 | °C | |
| RTIElec | 6.0mm | UL746 | 125 | °C | |
| RTIImp | 0.8mm | UL746 | 65.0 | °C | |
| RTIImp | 1.5mm | UL746 | 75.0 | °C | |
| RTIImp | 3.0mm | UL746 | 75.0 | °C | |
| RTIImp | 6.0mm | UL746 | 75.0 | °C | |
| RTI | 0.8mm | UL746 | 65.0 | °C | |
| RTI | 1.5mm | UL746 | 85.0 | °C | |
| RTI | 3.0mm | UL746 | 85.0 | °C | |
| RTI | 6.0mm | UL746 | 85.0 | °C | |
| 体积电阻率 | ASTMD257 | 1.0E+14 | ohmscm | ||
| 介电强度(0.800mm) | ASTMD149 | 30 | kV/mm | ||
| 相比耐漏电起痕指数(CTI)(0.800mm) | UL746 | PLC0 | |||
| 高电弧燃烧指数(HAI) | 0.8mm | UL746 | PLC0 | ||
| 高电弧燃烧指数(HAI) | 1.5mm | UL746 | PLC0 | ||
| 高电弧燃烧指数(HAI) | 3.0mm | UL746 | PLC0 | ||
| 高电弧燃烧指数(HAI) | 6.0mm | UL746 | PLC0 | ||
| 高电压电弧起痕速率(HVTR)(0.800mm) | UL746 | PLC1 | |||
| 热丝引燃(HWI) | 0.8mm | UL746 | PLC4 | ||
| 热丝引燃(HWI) | 1.5mm | UL746 | PLC4 | ||
| 热丝引燃(HWI) | 3.0mm | UL746 | PLC3 | ||
| 热丝引燃(HWI) | 6.0mm | UL746 | PLC2 | ||
| UL阻燃等级 | 0.8mm | UL94 | V-2 | ||
| UL阻燃等级 | 1.5mm | UL94 | V-2 | ||
| UL阻燃等级 | 3.0mm | UL94 | V-2 | ||
| UL阻燃等级 | 6.0mm | UL94 | V-2 | ||
| 关于美国Polymer Resources PRL NY6-GP2价格 | |||||
| 1.有关“PA6 美国Polymer Resources PRL NY6-GP2”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||