| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.44 | g/cm3 | ||
| 密度 | ISO1183 | 1.44 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 1.0 | % | |||
| 吸水率(饱和) | ASTMD570 | 4.9 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 4.9 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 1.4 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 1.4 | % | ||
| 拉伸模量(23°C) | ISO527-2 | 4330 | MPa | ||
| 抗张强度(屈服,23°C) | ASTMD638 | 64.0 | MPa | ||
| 拉伸应力(屈服,23°C) | ISO527-2 | 65.0 | MPa | ||
| 抗张强度(断裂,23°C) | ASTMD638 | 62.0 | MPa | ||
| 伸长率(屈服,23°C) | ASTMD638 | 3.0 | % | ||
| 拉伸应变(屈服,23°C) | ISO527-2 | 3.0 | % | ||
| 伸长率(断裂,23°C) | ASTMD638 | 15 | % | ||
| 弯曲模量 | -40°C | ASTMD790 | 5230 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 4000 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 1250 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 770 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 750 | MPa | |
| 弯曲强度 | -40°C | ASTMD790 | 180 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 109 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 45.0 | MPa | |
| 弯曲强度 | 90°C | ASTMD790 | 30.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 30.0 | MPa | |
| 简支梁缺口冲击强度 | -30°C | ISO179 | 3.0 | kJ/m2 | |
| 简支梁缺口冲击强度 | 23°C | ISO179 | 6.0 | kJ/m2 | |
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 86 | J/m | ||
| 落下冲击阻力(23°C) | InternalMethod | 74.6 | J | ||
| 洛氏硬度(R级) | ASTMD785 | 119 | |||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 80.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 溶融温度（DSC） | ISO3146 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 2.3E-5 | cm/cm/°C | ||
| RTIElec | 0.75mm | UL746 | 65.0 | °C | |
| RTIElec | 1.5mm | UL746 | 65.0 | °C | |
| RTIElec | 3.0mm | UL746 | 65.0 | °C | |
| RTIImp | 0.75mm | UL746 | 65.0 | °C | |
| RTIImp | 1.5mm | UL746 | 65.0 | °C | |
| RTIImp | 3.0mm | UL746 | 65.0 | °C | |
| RTIStr | 0.75mm | UL746 | 65.0 | °C | |
| RTIStr | 1.5mm | UL746 | 65.0 | °C | |
| RTIStr | 3.0mm | UL746 | 65.0 | °C | |
| VolumeResistivity(1.50mm) | ASTMD257 | >1.0E+13 | ohmscm | ||
| 体积电阻率 | IEC60093 | >1.0E+13 | ohmscm | ||
| UL阻燃等级 | 0.75mm | UL94 | HB | ||
| UL阻燃等级 | 1.5mm | UL94 | HB | ||
| UL阻燃等级 | 3.0mm | UL94 | HB | ||
| 关于德国巴斯夫 Ultramid® HPN 9362价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® HPN 9362”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-23122-0.htmlPA6 德国巴斯夫 Ultramid® HPN 9362
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。