| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 密度 | ISO1183 | 1.13 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 1.2 | % | |||
| 吸水率(24hr) | ASTMD570 | 1.6 | % | ||
| 吸水率(23°C,24hr) | ISO62 | 1.6 | % | ||
| 吸水率(饱和) | ASTMD570 | 9.5 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 9.5 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 2.7 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 2.7 | % | ||
| 拉伸模量 | 23°C | ISO527-2 | 2700 | MPa | |
| 拉伸模量 | 80°C | ISO527-2 | 485 | MPa | |
| 拉伸模量 | 120°C | ISO527-2 | 360 | MPa | |
| 拉伸模量 | 150°C | ISO527-2 | 290 | MPa | |
| 抗张强度 | 屈服,-40°C | ASTMD638 | 126 | MPa | |
| 抗张强度 | 屈服,23°C | ASTMD638 | 79.0 | MPa | |
| 抗张强度 | 屈服,80°C | ASTMD638 | 35.0 | MPa | |
| 抗张强度 | Yield,121°C | ASTMD638 | 25.0 | MPa | |
| 拉伸应力 | 屈服,-40°C | ISO527-2 | 126 | MPa | |
| 拉伸应力 | 屈服,23°C | ISO527-2 | 78.0 | MPa | |
| 拉伸应力 | 屈服,80°C | ISO527-2 | 35.0 | MPa | |
| 拉伸应力 | 屈服,120°C | ISO527-2 | 25.0 | MPa | |
| 拉伸应力 | 屈服,150°C | ISO527-2 | 20.0 | MPa | |
| 抗张强度(断裂,23°C) | ASTMD638 | 75.0 | MPa | ||
| 伸长率 | 屈服,23°C | ASTMD638 | 4.0 | % | |
| 伸长率 | 屈服,80°C | ASTMD638 | 42 | % | |
| 伸长率 | Yield,121°C | ASTMD638 | 36 | % | |
| 拉伸应变(屈服,23°C) | ISO527-2 | 4.0 | % | ||
| 伸长率(断裂,23°C) | ASTMD638 | 55 | % | ||
| 标称拉伸断裂应变(23°C) | ISO527-2 | 25 | % | ||
| 弯曲模量 | -40°C | ASTMD790 | 3010 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 2830 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 500 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 350 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 305 | MPa | |
| 弯曲模量(23°C) | ISO178 | 2400 | MPa | ||
| 弯曲强度 | -40°C | ASTMD790 | 170 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 108 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 30.0 | MPa | |
| 弯曲强度 | 90°C | ASTMD790 | 20.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 17.0 | MPa | |
| 弯曲应力(23°C) | ISO178 | 85.0 | MPa | ||
| 简支梁缺口冲击强度(23°C) | ISO179 | 3.5 | kJ/m2 | ||
| 简支梁无缺口冲击强度 | -30°C | ISO179 | 51 | kJ/m2 | |
| 简支梁无缺口冲击强度 | 23°C | ISO179 | NoBreak | ||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 48 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 58 | J/m | |
| 落下冲击阻力(23°C) | InternalMethod | 142 | J | ||
| 洛氏硬度(R级) | ASTMD785 | 119 | |||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 178 | °C | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/B | 150 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 65.0 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 60.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 溶融温度（DSC） | ISO3146 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 8.3E-5 | cm/cm/°C | ||
| RTIElec | 0.71mm | UL746 | 130 | °C | |
| RTIElec | 1.5mm | UL746 | 130 | °C | |
| RTIElec | 3.0mm | UL746 | 130 | °C | |
| RTIElec | 6.0mm | UL746 | 130 | °C | |
| RTIImp | 0.71mm | UL746 | 95.0 | °C | |
| RTIImp | 1.5mm | UL746 | 105 | °C | |
| RTIImp | 3.0mm | UL746 | 105 | °C | |
| RTIImp | 6.0mm | UL746 | 105 | °C | |
| 关于德国巴斯夫 Ultramid® 8202 HS价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8202 HS”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||