| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.14到1.15 | g/cm3 | ||
| 吸水率 | 24hr | ASTMD570 | 0.50到0.60 | % | |
| 吸水率 | 饱和 | ASTMD570 | 2.0到2.5 | % | |
| 吸水率 | PVLimit-Unlubed2 | ASTMD570 | 110 | MPa | |
| 洛氏硬度(R级) | ASTMD785 | 100到115 | |||
| 拉伸模量 | ASTMD638 | 2590到3280 | MPa | ||
| 抗张强度 | ASTMD638 | 65.5到75.8 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 45到55 | % | ||
| 弯曲模量 | ASTMD790 | 2590到3280 | MPa | ||
| 弯曲强度 | ASTMD790 | 96.5到110 | MPa | ||
| 压缩模量 | ASTMD695 | 1900到2590 | MPa | ||
| 压缩强度(10%应变) | ASTMD695 | 82.7到96.5 | MPa | ||
| 剪切强度 | ASTMD732 | 55.2到62.1 | MPa | ||
| 摩擦系数(与自身-动态) | ASTMD1894 | 0.12 | |||
| 负载变形 | ASTMD621 | 0.700到0.800 | % | ||
| 磨损因数-K | 4.00 | ||||
| 悬壁梁缺口冲击强度 | ASTMD256 | 75到96 | J/m | ||
| 拉伸冲击强度 | ASTMD1822 | 69.4到75.7 | kJ/m2 | ||
| 载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648 | 204到221 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648 | 93.3到204 | °C | |
| 连续使用温度 | ASTMD794 | 110 | °C | ||
| 熔融温度 | 227到238 | °C | |||
| 线形热膨胀系数-流动 | ASTMD696 | 9.0E-5 | cm/cm/°C | ||
| ServiceTemperature-Intermittent | 166 | °C | |||
| 关于美国Cast Nylons Nycast Nyloil价格 | |||||
| 1.有关“PA6 美国Cast Nylons Nycast Nyloil”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-23228-0.htmlPA6 美国Cast Nylons Nycast Nyloil
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。