| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.25 | g/cm3 | ||
| 密度 | ASTMD792 | 1.25 | g/cm3 | ||
| 密度 | ISO1183 | 1.24 | g/cm3 | ||
| 收缩率-流量(24小时) | ASTMD955 | 0.50to0.70 | % | ||
| MoldingShrinkage-AcrossFlow(24hr) | ASTMD955 | 0.90to2.0 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 6.6 | % | ||
| 拉伸模量2 | ASTMD638 | 5620 | MPa | ||
| 拉伸模量 | ISO527-2/1 | 4750 | MPa | ||
| 抗张强度3(屈服) | ASTMD638 | 82.0 | MPa | ||
| 拉伸应力(屈服) | ISO527-2/5 | 72.0 | MPa | ||
| 抗张强度3(断裂) | ASTMD638 | 74.0 | MPa | ||
| 拉伸应力(断裂) | ISO527-2/5 | 68.0 | MPa | ||
| 伸长率3(屈服) | ASTMD638 | 2.3 | % | ||
| 拉伸应变(屈服) | ISO527-2/5 | 2.4 | % | ||
| 伸长率4(断裂) | ASTMD638 | 2.4 | % | ||
| 拉伸应变(断裂) | ISO527-2/5 | 2.8 | % | ||
| 弯曲模量4(50.0mm跨距) | ASTMD790 | 4250 | MPa | ||
| 弯曲模量5 | ISO178 | 4260 | MPa | ||
| 弯曲应力 | ISO178 | 103 | MPa | ||
| 弯曲强度4(屈服,50.0mm跨距) | ASTMD790 | 121 | MPa | ||
| 弯曲强度5(断裂,50.0mm跨距) | ASTMD790 | 120 | MPa | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 93 | J/m | ||
| 悬壁梁缺口冲击强度6(23°C) | ISO180/1A | 9.3 | kJ/m2 | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD4812 | 750 | J/m | ||
| 无缺口伊佐德冲击强度5(23°C) | ISO180/1U | 44 | kJ/m2 | ||
| 装有测量仪表的落镖冲击(23°C,TotalEnergy) | ASTMD3763 | 10.5 | J | ||
| 多轴向仪器化冲击能量 | ISO6603-2 | 2.90 | J | ||
| 载荷下热变形温度(0.45MPa,未退火,3.20mm) | ASTMD648 | 207 | °C | ||
| HeatDeflectionTemperature7(0.45MPa,Unannealed,64.0mmSpan) | ISO75-2/Bf | 204 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火,3.20mm) | ASTMD648 | 188 | °C | ||
| 热变形温度7(1.8MPa,未退火,64.0mm跨距) | ISO75-2/Af | 181 | °C | ||
| 线形热膨胀系数-流动(-30到30°C) | ASTMD696 | 3.1E-5 | cm/cm/°C | ||
| CLTE-Transverse(-30to30°C) | ASTMD696 | 1.4E-4 | cm/cm/°C | ||
| 表面电阻率 | ASTMD257 | 9.0to11 | ohms | ||
| 关于沙伯基础 LNP™ STAT-LOY™ PF303 compound价格 | |||||
| 1.有关“PA6 沙伯基础 LNP™ STAT-LOY™ PF303 compound”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-23523-0.htmlPA6 沙伯基础 LNP™ STAT-LOY™ PF303 compound
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。