| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ASTMD1505 | 1.13 | g/cm3 | ||
| 熔流率（熔体流动速率）(235°C/1.0kg) | ASTMD1238 | 4.5 | g/10min | ||
| 吸水率 | 24hr | ASTMD570 | 1.6 | % | |
| 吸水率 | 饱和 | ASTMD570 | 9.5 | % | |
| 吸水率 | 平衡 | ASTMD570 | 2.7 | % | |
| MoistureContent | ASTMD6869 | >800 | ppm | ||
| 相对粘度 83aec3bab5>[email protected]%SulfuricAcid | 3.01 | ||||
| 粘度-FAV | ASTMD789 | 73.0 | |||
| 薄膜厚度-经测试 | 51 | um | |||
| 弹性模量-MD2 | ASTMD882 | 710 | MPa | ||
| 弹性模量-TD2 | ASTMD882 | 620 | MPa | ||
| 抗张强度2 | MD:屈服 | ASTMD882 | 40.0 | MPa | |
| 抗张强度2 | TD:屈服 | ASTMD882 | 30.0 | MPa | |
| 抗张强度2 | MD:断裂 | ASTMD882 | 90.0 | MPa | |
| 抗张强度2 | TD:断裂 | ASTMD882 | 90.0 | MPa | |
| 伸长率2 | MD:断裂 | ASTMD882 | 340 | % | |
| 伸长率2 | TD:断裂 | ASTMD882 | 360 | % | |
| 二氧化碳传输速率(23°C) | ASTMD1434 | 72.8 | cm3/m2/24hr | ||
| 氮传输速率(23°C) | ASTMD1434 | 14.0 | cm3/m2/24hr | ||
| 氧气传输速率(23°C) | ASTMD3985 | 40 | cm3/m2/24hr | ||
| 水气透过率(38°C,100%RH) | ASTMF1249 | 990 | gmm/m2/atm/24hr | ||
| ElmendorfTearStrength | MD:23°C | ASTMD1922 | 590 | N | |
| ElmendorfTearStrength | TD:23°C | ASTMD1922 | 530 | N | |
| GravesTear | MD:23°C | ASTMD1004 | 3530 | N | |
| GravesTear | TD:23°C | ASTMD1004 | 3290 | N | |
| 薄膜厚度-经测试 | 51 | um | |||
| 弹性模量-MD2 | ASTMD882 | 710 | MPa | ||
| 弹性模量-TD2 | ASTMD882 | 620 | MPa | ||
| 抗张强度2 | MD:屈服 | ASTMD882 | 40.0 | MPa | |
| 抗张强度2 | TD:屈服 | ASTMD882 | 30.0 | MPa | |
| 抗张强度2 | MD:断裂 | ASTMD882 | 90.0 | MPa | |
| 抗张强度2 | TD:断裂 | ASTMD882 | 90.0 | MPa | |
| 伸长率2 | MD:断裂 | ASTMD882 | 340 | % | |
| 伸长率2 | TD:断裂 | ASTMD882 | 360 | % | |
| 二氧化碳传输速率(23°C) | ASTMD1434 | 72.8 | cm3/m2/24hr | ||
| 氮传输速率(23°C) | ASTMD1434 | 14.0 | cm3/m2/24hr | ||
| 氧气传输速率(23°C) | ASTMD3985 | 40 | cm3/m2/24hr | ||
| 水气透过率(38°C,100%RH) | ASTMF1249 | 990 | gmm/m2/atm/24hr | ||
| ElmendorfTearStrength | MD:23°C | ASTMD1922 | 590 | N | |
| ElmendorfTearStrength | TD:23°C | ASTMD1922 | 530 | N | |
| GravesTear | MD:23°C | ASTMD1004 | 3530 | N | |
| GravesTear | TD:23°C | ASTMD1004 | 3290 | N | |
| 熔融温度 | 220 | °C | |||
| PunctureIndex3(23°C) | 193.4 | kN/m | |||
| PunctureResistance3(23°C) | 1000 | g | |||
| 关于美国Honeywell Aegis® H73ZP价格 | |||||
| 1.有关“PA6 美国Honeywell Aegis® H73ZP”物性表及PA6塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料的需求请与我们联系. | |||||