| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.62 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 0.30 | % | |||
| 吸水率(24hr) | ASTMD570 | 0.90 | % | ||
| 吸水率(饱和) | ASTMD570 | 4.0 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 1.1 | % | ||
| 抗张强度(断裂,23°C) | ASTMD638 | 157 | MPa | ||
| 伸长率(断裂,23°C) | ASTMD638 | 3.0 | % | ||
| 弯曲模量(23°C) | ASTMD790 | 8970 | MPa | ||
| 弯曲强度(23°C) | ASTMD790 | 232 | MPa | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 110 | J/m | ||
| 洛氏硬度(R级) | ASTMD785 | 121 | |||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 195 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| RTIElec | 0.8mm | UL746 | 130 | °C | |
| RTIElec | 1.5mm | UL746 | 130 | °C | |
| RTIElec | 2.5mm | UL746 | 130 | °C | |
| RTIElec | 3.0mm | UL746 | 130 | °C | |
| RTIImp | 0.8mm | UL746 | 105 | °C | |
| RTIImp | 1.5mm | UL746 | 115 | °C | |
| RTIImp | 2.5mm | UL746 | 115 | °C | |
| RTIImp | 3.0mm | UL746 | 115 | °C | |
| RTIStr | 0.8mm | UL746 | 105 | °C | |
| RTIStr | 1.5mm | UL746 | 115 | °C | |
| RTIStr | 2.5mm | UL746 | 115 | °C | |
| RTIStr | 3.0mm | UL746 | 120 | °C | |
| VolumeResistivity(1.50mm) | ASTMD257 | >1.0E+13 | ohmscm | ||
| DielectricStrength2(1.50mm) | ASTMD149 | 29 | kV/mm | ||
| UL阻燃等级 | 0.8mm | UL94 | V-0 | ||
| UL阻燃等级 | 1.5mm | UL94 | V-0 | ||
| UL阻燃等级 | 2.5mm | UL94 | V-05VA | ||
| UL阻燃等级 | 3.0mm | UL94 | V-05VA | ||
| 关于德国巴斯夫 Ultramid® 8232G HS FR价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8232G HS FR”物性表及PA6塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-41-24528-0.htmlPA6 德国巴斯夫 Ultramid® 8232G HS FR