| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.14到1.16 | g/cm3 | ||
| 吸水率 | 24hr | ASTMD570 | 0.50到0.60 | % | |
| 吸水率 | 饱和 | ASTMD570 | 5.0到6.0 | % | |
| 洛氏硬度(R级) | ASTMD785 | 110到115 | |||
| 肖氏硬度(邵氏D) | ASTMD2240 | 76到78 | |||
| 拉伸模量 | ASTMD638 | 2590到3030 | MPa | ||
| 抗张强度 | ASTMD638 | 66.9到74.5 | MPa | ||
| 伸长率(断裂) | ASTMD638 | 25到35 | % | ||
| 弯曲模量 | ASTMD790 | 2280到2410 | MPa | ||
| 弯曲强度 | ASTMD790 | 82.7到89.6 | MPa | ||
| 压缩模量 | ASTMD695 | 1930到2380 | MPa | ||
| 压缩强度(10%应变) | ASTMD695 | 86.2到104 | MPa | ||
| 剪切强度 | ASTMD732 | 68.9到75.8 | MPa | ||
| 负载变形 | ASTMD621 | 1.00到2.00 | % | ||
| 悬壁梁缺口冲击强度 | ASTMD256 | 44到49 | J/m | ||
| 载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648 | 204到221 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648 | 93.3到204 | °C | |
| 载荷下热变形温度 | 连续使用温度 | ASTMD648 | 110 | °C | |
| 载荷下热变形温度 | 熔融温度 | ASTMD648 | 227到238 | °C | |
| 线形热膨胀系数-流动 | ASTMD696 | 9.0E-5 | cm/cm/°C | ||
| ServiceTemperature-Intermittent | 166 | °C | |||
| 介电强度 | ASTMD149 | 20到24 | kV/mm | ||
| 介电常数 | 60Hz | ASTMD150 | 3.70 | ||
| 介电常数 | 1kHz | ASTMD150 | 3.70 | ||
| 介电常数 | 100kHz | ASTMD150 | 3.70 | ||
| 关于美国Cast Nylons Nycast Nymetal 6MPY价格 | |||||
| 1.有关“PA6 美国Cast Nylons Nycast Nymetal 6MPY”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-24676-0.htmlPA6 美国Cast Nylons Nycast Nymetal 6MPY
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。