| 中等粘性,阻燃性 注射成型 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ISO1183/A | 1.26 | g/cm3 | ||
| 粘数 | ISO307 | 145 | cm3/g | ||
| 拉伸模量 | ISO527-2/1A/1 | 3800 | MPa | ||
| 拉伸应力(屈服) | ISO527-2/1A/50 | 70.0 | MPa | ||
| 拉伸应变(屈服) | ISO527-2/1A/50 | 3.0 | % | ||
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 3.0 | kJ/m2 | |
| 简支梁缺口冲击强度 | 23°C | ISO179/1eA | 4.0 | kJ/m2 | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 48 | kJ/m2 | |
| 简支梁无缺口冲击强度 | 23°C | ISO179/1eU | 49 | kJ/m2 | |
| 球压硬度(H358/30) | ISO2039-1 | 160 | MPa | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/Bf | 186 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/Af | 76.0 | °C | ||
| 维卡软化温度 | ―― | ISO306/A50 | 217 | °C | |
| 维卡软化温度 | ―― | ISO306/B50 | 202 | °C | |
| BallPressureTest(200°C) | IEC60695-10-2 | Pass | |||
| RTIElec | 0.38mm | UL746 | 130 | °C | |
| RTIElec | 0.75mm | UL746 | 130 | °C | |
| RTIElec | 1.5mm | UL746 | 130 | °C | |
| RTIElec | 3.0mm | UL746 | 130 | °C | |
| RTIImp | 0.38mm | UL746 | 75.0 | °C | |
| RTIImp | 0.75mm | UL746 | 90.0 | °C | |
| RTIImp | 1.5mm | UL746 | 100 | °C | |
| RTIImp | 3.0mm | UL746 | 100 | °C | |
| RTIStr | 0.38mm | UL746 | 100 | °C | |
| RTIStr | 0.75mm | UL746 | 110 | °C | |
| RTIStr | 1.5mm | UL746 | 120 | °C | |
| RTIStr | 3.0mm | UL746 | 120 | °C | |
| 漏电起痕指数 | IEC60112 | 300 | V | ||
| 高电弧燃烧指数(HAI) | 0.38mm | UL746 | PLC0 | ||
| 高电弧燃烧指数(HAI) | 0.75mm | UL746 | PLC0 | ||
| 高电弧燃烧指数(HAI) | 1.5mm | UL746 | PLC0 | ||
| 高电弧燃烧指数(HAI) | 3.0mm | UL746 | PLC0 | ||
| 热丝引燃(HWI) | 0.38mm | UL746 | PLC4 | ||
| 热丝引燃(HWI) | 0.75mm | UL746 | PLC4 | ||
| 热丝引燃(HWI) | 1.5mm | UL746 | PLC2 | ||
| 热丝引燃(HWI) | 3.0mm | UL746 | PLC0 | ||
| 燃烧速率 | 0.380mm,Self-Extinguishing | ISO3795 | 0.0 | mm/min | |
| 燃烧速率 | 0.750mm,Self-Extinguishing | ISO3795 | 0.0 | mm/min | |
| 燃烧速率 | 1.50mm,自动灭火 | ISO3795 | 0.0 | mm/min | |
| 燃烧速率 | 3.00mm,自动灭火 | ISO3795 | 0.0 | mm/min | |
| UL阻燃等级 | 0.38mm | UL94 | V-2 | ||
| UL阻燃等级 | 0.75mm | UL94 | V-2 | ||
| UL阻燃等级 | 1.5mm | UL94 | V-2 | ||
| UL阻燃等级 | 3.0mm | UL94 | V-2 | ||
| FlammabilityClassification | 0.38mm | IEC60695-11-10,-20 | V-2 | ||
| FlammabilityClassification | 0.75mm | IEC60695-11-10,-20 | V-2 | ||
| FlammabilityClassification | 1.5mm | IEC60695-11-10,-20 | V-2 | ||
| FlammabilityClassification | 3.0mm | IEC60695-11-10,-20 | V-2 | ||
| 灼热丝易燃指数 | 0.38mm | IEC60695-2-12 | 850 | °C | |
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 850 | °C | |
| 灼热丝易燃指数 | 1.5mm | IEC60695-2-12 | 960 | °C | |
| 灼热丝易燃指数 | 3.0mm | IEC60695-2-12 | 960 | °C | |
| 热灯丝点火温度 | 0.38mm | IEC60695-2-13 | 825 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 825 | °C | |
| 热灯丝点火温度 | 1.5mm | IEC60695-2-13 | 825 | °C | |
| 热灯丝点火温度 | 3.0mm | IEC60695-2-13 | 825 | °C | |
| 极限氧指数 | ISO4589-2 | 23 | % | ||
| 关于美国舒尔曼 SCHULAMID® 6 MV 14 FR 4 K1681价格 | |||||
| 1.有关“PA6 美国舒尔曼 SCHULAMID® 6 MV 14 FR 4 K1681”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-24788-0.htmlPA6 美国舒尔曼 SCHULAMID® 6 MV 14 FR 4 K1681
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。