| 低翘曲性,热稳定性,可加工性，良好,高强度,刚性，高,韧性良好,尺寸稳定性良好 注射成型 | 黑色,自然色 |
| 填料：Chem Polymer公司。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.50 | g/cm3 | ||
| 收缩率-流动 | ASTMD955 | 0.15to0.40 | % | ||
| 吸水率(24hr) | ASTMD570 | 0.90 | % | ||
| 抗张强度 | ASTMD638 | 128 | MPa | ||
| 伸长率(屈服) | ASTMD638 | 2.5 | % | ||
| 伸长率(断裂) | ASTMD638 | 2.5 | % | ||
| 弯曲模量 | ASTMD790 | 7580 | MPa | ||
| 弯曲强度 | ASTMD790 | 190 | MPa | ||
| 悬壁梁缺口冲击强度(23°C) | ASTMD256 | 85 | J/m | ||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 213 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 205 | °C | ||
| 熔融温度 | 216 | °C | |||
| 线形热膨胀系数-流动 | ASTMD696 | 5.5E-5 | cm/cm/°C | ||
| RTIElec | 0.8mm | UL746 | 65.0 | °C | |
| RTIElec | 1.5mm | UL746 | 65.0 | °C | |
| RTIElec | 3.0mm | UL746 | 65.0 | °C | |
| RTIImp | 0.8mm | UL746 | 65.0 | °C | |
| RTIImp | 1.5mm | UL746 | 65.0 | °C | |
| RTIImp | 3.0mm | UL746 | 65.0 | °C | |
| RTIStr | 0.8mm | UL746 | 65.0 | °C | |
| RTIStr | 1.5mm | UL746 | 65.0 | °C | |
| RTIStr | 3.0mm | UL746 | 65.0 | °C | |
| 体积电阻率 | ASTMD257 | 1.0E+14 | ohmscm | ||
| 介电强度(3.00mm) | ASTMD149 | 12 | kV/mm | ||
| 相比耐漏电起痕指数(CTI) | UL746 | 500 | V | ||
| UL阻燃等级(0.8mm) | UL94 | HB | |||
| 极限氧指数 | ASTMD2863 | 24 | % | ||
| 关于Chem Polymer公司 Chemlon® 225-15 MGH价格 | |||||
| 1.有关“PA6 Chem Polymer公司 Chemlon® 225-15 MGH”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-24796-0.htmlPA6 Chem Polymer公司 Chemlon® 225-15 MGH
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。