| 注射成型 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 密度 | ISO1183/A | 1.26 | g/cm3 | ||
| 粘数 | ISO307 | 129 | cm3/g | ||
| 拉伸模量 | ISO527-2/1A/1 | 3200 | MPa | ||
| 拉伸应力(屈服) | ISO527-2/1A/50 | 60.0 | MPa | ||
| 拉伸应变(屈服) | ISO527-2/1A/50 | 3.3 | % | ||
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 4.3 | kJ/m2 | |
| 简支梁缺口冲击强度 | 23°C | ISO179/1eA | 4.7 | kJ/m2 | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 38 | kJ/m2 | |
| 简支梁无缺口冲击强度 | 23°C | ISO179/1eU | 40 | kJ/m2 | |
| 热变形温度(0.45MPa,未退火) | ISO75-2/Bf | 178 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/Af | 56.0 | °C | ||
| 维卡软化温度 | ―― | ISO306/A50 | 211 | °C | |
| 维卡软化温度 | ―― | ISO306/B50 | 195 | °C | |
| 漏电起痕指数 | IEC60112 | 300 | V | ||
| UL阻燃等级 | 0.40mm | UL94 | V-2 | ||
| UL阻燃等级 | 0.8mm | UL94 | V-2 | ||
| UL阻燃等级 | 1.6mm | UL94 | V-2 | ||
| UL阻燃等级 | 3.2mm | UL94 | V-2 | ||
| FlammabilityClassification | 0.40mm | IEC60695-11-10,-20 | V-2 | ||
| FlammabilityClassification | 0.8mm | IEC60695-11-10,-20 | V-2 | ||
| FlammabilityClassification | 1.6mm | IEC60695-11-10,-20 | V-2 | ||
| FlammabilityClassification | 3.2mm | IEC60695-11-10,-20 | V-2 | ||
| 灼热丝易燃指数 | 0.38mm | IEC60695-2-12 | 960 | °C | |
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 930 | °C | |
| 灼热丝易燃指数 | 1.5mm | IEC60695-2-12 | 960 | °C | |
| 灼热丝易燃指数 | 3.0mm | IEC60695-2-12 | 960 | °C | |
| 热灯丝点火温度 | 0.38mm | IEC60695-2-13 | 930 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 930 | °C | |
| 热灯丝点火温度 | 1.5mm | IEC60695-2-13 | 825 | °C | |
| 热灯丝点火温度 | 3.0mm | IEC60695-2-13 | 825 | °C | |
| 极限氧指数 | ISO4589-2 | 22 | % | ||
| 关于美国舒尔曼 SCHULAMID® 6 MV 14 FR 4 K1681 BLACK 96.8076价格 | |||||
| 1.有关“PA6 美国舒尔曼 SCHULAMID® 6 MV 14 FR 4 K1681 BLACK 96.8076”物性表及PA6塑胶原料价格以出厂实时数据为准. 2.更多塑胶原料的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-41-25060-0.htmlPA6 美国舒尔曼 SCHULAMID® 6 MV 14 FR 4 K1681 BLACK 96.8076
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。