| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 密度 | ISO1183 | 1.14 | g/cm3 | ||
| 收缩率-流动 | ASTMD955 | 0.20to0.40 | % | ||
| 收缩率-流动 | ISO294-4 | 0.20to0.40 | % | ||
| 抗张强度 | ASTMD638 | 91.7 | MPa | ||
| TensileStress(4.00mm) | ISO527-2 | 92.0 | MPa | ||
| 拉伸应变(断裂,4.00mm) | ISO527-2 | 10 | % | ||
| 弯曲模量(4.00mm) | ASTMD790 | 4960 | MPa | ||
| 弯曲模量(4.00mm) | ISO178 | 5000 | MPa | ||
| CharpyNotchedImpactStrength2 | -20°C | ASTMD256 | 2.1 | kJ/m2 | |
| CharpyNotchedImpactStrength2 | -20°C | ISO179 | 3.0 | kJ/m2 | |
| CharpyNotchedImpactStrength2 | 23°C | ISO179 | 7.0 | kJ/m2 | |
| CharpyNotchedImpactStrength2 | 23°C | ASTMD256 | 6.3 | kJ/m2 | |
| 简支梁无缺口冲击强度2 | -20°C | ASTMD256 | 8.4 | kJ/m2 | |
| 简支梁无缺口冲击强度2 | -20°C | ISO179 | 10 | kJ/m2 | |
| 简支梁无缺口冲击强度2 | 23°C | ISO179 | 20 | kJ/m2 | |
| 简支梁无缺口冲击强度2 | 23°C | ASTMD256 | 19 | kJ/m2 | |
| NotchedIzodImpact(Area) | -20°C,4.00mm | ASTMD256 | 8.41 | kJ/m2 | |
| NotchedIzodImpact(Area) | 23°C,4.00mm | ASTMD256 | 8.41 | kJ/m2 | |
| 悬壁梁缺口冲击强度2 | -20°C | ISO180 | 8.0 | kJ/m2 | |
| 悬壁梁缺口冲击强度2 | 23°C | ISO180 | 9.0 | kJ/m2 | |
| 无缺口悬臂梁冲击 | -20°C,4.00mm | ASTMD256 | 37.8 | kJ/m2 | |
| 无缺口悬臂梁冲击 | 23°C,4.00mm | ASTMD256 | 39.9 | kJ/m2 | |
| 无缺口伊佐德冲击强度2 | -20°C | ISO180 | 38 | kJ/m2 | |
| 无缺口伊佐德冲击强度2 | 23°C | ISO180 | 40 | kJ/m2 | |
| 肖氏硬度(邵氏D) | ISO868 | 82 | |||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648B | 214 | °C | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/Bf | 214 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648A | 193 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/Af | 193 | °C | ||
| 维卡软化温度 | ASTMD15253 | 217 | °C | ||
| 维卡软化温度 | ISO306/A50 | 217 | °C | ||
| 表面电阻率 | IEC61340-2-3 | <1.0E+7 | ohms | ||
| 体积电阻率 | InternalMethod | <1.0E+5 | ohmscm | ||
| 关于芬兰普宓斯 PRE-ELEC® PA 1406价格 | |||||
| 1.有关“PA6 芬兰普宓斯 PRE-ELEC® PA 1406”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-25132-0.htmlPA6 芬兰普宓斯 PRE-ELEC® PA 1406
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。