| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792,ISO1183 | 1.16 | g/cm3 | ||
| 吸水率 | 24hr | ASTMD570 | 1.0 | % | |
| 吸水率 | 23°C,24hr | ISO62 | 1.0 | % | |
| 拉伸应力 | 断裂 | ISO527-2 | 80.0 | MPa | |
| 拉伸应力 | ―― | ASTMD638 | 80.0 | MPa | |
| 伸长率(断裂) | ASTMD638,ISO527-2 | 25 | % | ||
| 弯曲模量 | ASTMD790,ISO178 | 3200 | MPa | ||
| 弯曲强度 | ASTMD790,ISO178 | 95.0 | MPa | ||
| 简支梁无缺口冲击强度 | ISO179 | 90 | kJ/m2 | ||
| 悬壁梁缺口冲击强度 | ISO180 | 3.5 | kJ/m2 | ||
| 载荷下热变形温度 | 0.45MPa,未退火 | ASTMD648,ISO75-2/B | 200 | °C | |
| 载荷下热变形温度 | 1.8MPa,未退火 | ASTMD648,ISO75-2/A | 75.0 | °C | |
| 熔融温度 | ISO1218,ASTMD2117 | 218 | °C | ||
| 线形热膨胀系数-流动 | ASTMD696 | 6.5E-5 | cm/cm/°C | ||
| 表面电阻率 | ASTMD257,IEC60093 | 1.0E+15 | ohms | ||
| 介电强度 | ASTMD149,IEC60243-1 | 37 | kV/mm | ||
| 漏电起痕指数 | 解决方案A | IEC60112 | 600 | V | |
| 漏电起痕指数 | ―― | ASTMD3638 | 600 | V | |
| UL阻燃等级(1.6mm) | UL94 | V-0 | |||
| 灼热丝易燃指数 | 0.75mm | IEC60695-2-12 | 850 | °C | |
| 灼热丝易燃指数 | 1.5mm | IEC60695-2-12 | 850 | °C | |
| 热灯丝点火温度 | 0.75mm | IEC60695-2-13 | 775 | °C | |
| 热灯丝点火温度 | 1.5mm | IEC60695-2-13 | 775 | °C | |
| 极限氧指数 | ASTMD2863,ISO4589-2 | >30 | % | ||
| 关于英国Jackdaw VITAMIDE® BF23OR6570价格 | |||||
| 1.有关“PA6 英国Jackdaw VITAMIDE® BF23OR6570”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-25574-0.htmlPA6 英国Jackdaw VITAMIDE® BF23OR6570
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。