| 其它 其它 注塑 | |
| 用于机械零件、消费用品等 | |
| 特性：改进机器进料和脱模特性。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % | |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 吸水率 | 饱和(23℃) | ASTM D-570 | DAM｜8.5 | % | |
| 吸水率 | 饱和(23℃) | 50%RH｜- | % | ||
| 比重 | ASTM D-792 | DAM｜1.14 | |||
| 比重 | ASTM D-792 | 50%RH｜1.14 | |||
| 泰伯磨耗量 | cs-17 Wheel,1000g | DAM｜- | mg/1000 cycles | ||
| 泰伯磨耗量 | cs-17 Wheel,1000g | 50%RH｜7 | mg/1000 cycles | ||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜53 | j/m | |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 50%RH｜112 | j/m | |
| 洛氏硬度M | ASTM D-785 | DAM｜M79 | |||
| 洛氏硬度M | ASTM D-785 | 50%RH｜M59 | |||
| 硬度计硬度 | ASTM D-676 | DAM｜89 | |||
| 硬度计硬度 | ASTM D-676 | 50%RH｜82 | |||
| 洛氏硬度R | ASTM D-785 | DAM｜R121 | |||
| 洛氏硬度R | ASTM D-785 | 50%RH｜R108 | |||
| 屈服强度 | 23℃ | DAM｜82.7 | MPa | ||
| 屈服强度 | 23℃ | 50%RH｜58.6 | MPa | ||
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜82.7 | MPa | |
| 拉伸强度 | 23℃ | ASTM D-638 | 50%RH｜77.2 | MPa | |
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜2827 | MPa | |
| 揉曲模量 | 23℃ | ASTM D-790 | 50%RH｜1207 | MPa | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜157 | KJ/m2 | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | 50%RH｜231 | KJ/m2 | |
| 1%形变时的压应力 | ASTM D-695 | DAM｜33.8 | MPa | ||
| 1%形变时的压应力 | ASTM D-695 | 50%RH｜- | MPa | ||
| 剪切强度 | 23℃ | ASTM D-732 | DAM｜66.2 | MPa | |
| 剪切强度 | 23℃ | ASTM D-732 | 50%RH｜- | MPa | |
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜60 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 50%RH｜≥300 | % | |
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | ||
| 屈服伸长率 | ASTM D-638 | 50%RH｜25 | % | ||
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM｜504 | KJ/m2 | |
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | 50%RH｜1470 | KJ/m2 | |
| 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜3.6 | ||
| 介电常数 | 106Hz(cps) | ASTM D-150 | 50%RH｜4.6 | ||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜0.01 | ||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | 50%RH｜0.2 | ||
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜3.9 | ||
| 介电常数 | 103Hz(cps) | ASTM D-150 | 50%RH｜7.0 | ||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | 50%RH｜0.1 | ||
| 耗散因数 | 103Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 耗散因数 | 103Hz(cps) | ASTM D-150 | 50%RH｜0.2 | ||
| 体积电阻率 | ASTM D-257 | DAM｜1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 50%RH｜1013 | Ω.cm | ||
| 介电常数 | 100Hz(cps) | ASTM D-150 | DAM｜4.0 | ||
| 介电常数 | 100Hz(cps) | ASTM D-150 | 50%RH｜8.0 | ||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 | % | |
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜90 | ℃ | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔点结晶 | ASTM D-2177 | DAM｜270 | ℃ | ||
| 熔点结晶 | ASTM D-2177 | 50%RH｜- | ℃ | ||
| UL可燃性导级 | UL 94 | DAM｜94 | |||
| UL可燃性导级 | UL 94 | 50%RH｜V-2 | |||
| 脆化温度 | ASTM D-746 | DAM｜-80 | ℃ | ||
| 脆化温度 | ASTM D-746 | 50%RH｜-65 | ℃ | ||
| 关于新加坡杜邦 101L价格 | |||||
| 1.有关“PA66 新加坡杜邦 101L”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26222-0.htmlPA66 新加坡杜邦 101L
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。