| 其它 其它 注塑 | |
| UL94 V-0等级 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 24hr | ASTM D-570 | DAM｜0.5 | % | |
| 吸水率 | 24hr | ASTM D-570 | 50%RH｜- | % | |
| 比重 | ASTM D-792 | DAM｜1.56 | |||
| 比重 | ASTM D-792 | 50%RH｜- | |||
| 模具收缩率 | 3.2mm,flow | ASTM D-792 | DAM｜0.4 | % | |
| 模具收缩率 | 3.2mm,flow | ASTM D-792 | 50%RH｜- | % | |
| 弯曲强度 | ASTM D-790 | DAM｜240 | MPa | ||
| 弯曲强度 | ASTM D-790 | 50%RH｜- | MPa | ||
| 断裂伸长率 | ASTM D-638 | DAM｜2.5 | % | ||
| 断裂伸长率 | ASTM D-638 | 50%RH｜4 | % | ||
| 拉伸强度 | ASTN D-638 | DAM｜169 | MPa | ||
| 拉伸强度 | ASTN D-638 | 50%RH｜134 | MPa | ||
| IZOD缺口冲击强度 | ASTM D-256 | DAM｜100 | J/m | ||
| IZOD缺口冲击强度 | ASTM D-256 | 50%RH｜105 | J/m | ||
| 弯曲模量 | ASTM D-790 | DAM｜8960 | MPa | ||
| 弯曲模量 | ASTM D-790 | 50%RH｜6900 | MPa | ||
| 介电强度 | 3.2mm | ASTM D-149 | DAM｜17.2 | kv/mm | |
| 介电强度 | 3.2mm | ASTM D-149 | 50%RH｜15.6 | kv/mm | |
| 体积电阻率 | ASTM D-257 | DAM｜1014 | Ω.m | ||
| 体积电阻率 | ASTM D-257 | 50%RH｜1011 | Ω.m | ||
| 介电常数 | 103Hz | ASTM D-150 | DAM｜3.6 | ||
| 介电常数 | 103Hz | ASTM D-150 | 50%RH｜5.1 | ||
| 损耗因数 | 103Hz | ASTM D-150 | DAM｜0.009 | ||
| 损耗因数 | 103Hz | ASTM D-150 | 50%RH｜0.113 | ||
| 介电常数 | 106Hz | ASTM D-150 | DAM｜3.5 | ||
| 介电常数 | 106Hz | ASTM D-150 | 50%RH｜3.8 | ||
| 损耗因数 | 106Hz | ASTM D-150 | DAM｜0.014 | ||
| 损耗因数 | 106Hz | ASTM D-150 | 50%RH｜0.041 | ||
| 表面电阻率 | ASTM D-257 | DAM｜1014 | |||
| 表面电阻率 | ASTM D-257 | 50%RH｜1011 | |||
| 热变形温度 | 0.45MPa | ASTM D-648 | DAM｜257 | ℃ | |
| 热变形温度 | 0.45MPa | ASTM D-648 | 50%RH｜- | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | DAM｜235 | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔点 | ASTM D-3418 | DAM｜262 | ℃ | ||
| 熔点 | ASTM D-3418 | 50%RH｜- | ℃ | ||
| 关于美国杜邦 FR50价格 | |||||
| 1.有关“PA66 美国杜邦 FR50”物性表及PA66塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26258-0.htmlPA66 美国杜邦 FR50