| 其它 其它 注塑 | |
| 特性：良好的热稳定性 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % | |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 吸水率 | 饱和(23℃) | ASTM D-570 | DAM｜7.0 | % | |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 比重 | ASTM D-792 | DAM｜1.09 | |||
| 比重 | ASTM D-792 | 50%RH｜1.09 | |||
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜80 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 50%RH｜270 | % | |
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜1965 | MPa | |
| 揉曲模量 | 23℃ | ASTM D-790 | 50%RH｜1103 | MPa | |
| 洛氏硬度M | ASTM D-785 | DAM｜M71 | |||
| 洛氏硬度M | ASTM D-785 | 50%RH｜M50 | |||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜230 | J/m | |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 50%RH｜240 | J/m | |
| 硬度计硬度 | ASTM D-676 | DAM｜83 | |||
| 硬度计硬度 | ASTM D-676 | 50%RH｜76 | |||
| 洛氏硬度R | ASTM D-785 | DAM｜R115 | |||
| 洛氏硬度R | ASTM D-785 | 50%RH｜R102 | |||
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | ||
| 屈服伸长率 | ASTM D-638 | 50%RH｜15 | % | ||
| 屈服强度 | 23℃ | DAM｜60.7 | MPa | ||
| 屈服强度 | 23℃ | 50%RH｜51.7 | MPa | ||
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM｜550 | KJ/m2 | |
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | 50%RH｜1680 | KJ/m2 | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜189 | KJ/m2 | |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | 50%RH｜265 | KJ/m2 | |
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜62.1 | MPa | |
| 拉伸强度 | 23℃ | ASTM D-638 | 50%RH｜51.7 | MPa | |
| 体积电阻率 | ASTM D-257 | DAM｜1013 | Ω.m | ||
| 体积电阻率 | ASTM D-257 | 50%RH｜1013 | Ω.m | ||
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜3.1 | ||
| 介电常数 | 100Hz(cps) | ASTM D-150 | 50%RH｜4.8 | ||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | 50%RH｜0.1 | ||
| 耗散因数 | 103Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 耗散因数 | 103Hz(cps) | ASTM D-150 | 50%RH｜0.11 | ||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | 50%RH｜0.10 | ||
| 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜2.9 | ||
| 介电常数 | 106Hz(cps) | ASTM D-150 | 50%RH｜3.3 | ||
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜230 | ℃ | |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| UL可燃性导级 | UL 94 | DAM｜94 | |||
| UL可燃性导级 | UL 94 | 50%RH｜HB | |||
| 熔点结晶 | ASTM D-2177 | DAM｜270 | ℃ | ||
| 熔点结晶 | ASTM D-2177 | 50%RH｜- | ℃ | ||
| 线性热膨胀系数 | ASTM D-696 | DAM｜7×10-5 | m/m/℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 50%RH｜- | m/m/℃ | ||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 | % | |
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | |
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜255 | ℃ | |
| 熔点 | Fisher Johns法 | ASTM D-789 | 50%RH｜255 | ℃ | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜75 | ℃ | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 脆化温度 | ASTM D-746 | DAM｜-104 | ℃ | ||
| 脆化温度 | ASTM D-746 | 50%RH｜-84 | ℃ | ||
| 需氧指数 | ASTM D-2863 | DAM｜19 | % | ||
| 需氧指数 | ASTM D-2863 | 50%RH｜20 | % | ||
| 关于美国杜邦 408HS价格 | |||||
| 1.有关“PA66 美国杜邦 408HS”物性表及PA66塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系. | |||||