| 其它 其它 其它 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 饱和(23℃) | ASTM D-570 | DAM｜8.5 | % | |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % | |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | |
| 比重 | ASTM D-792 | DAM｜1.15 | |||
| 比重 | ASTM D-792 | 50%RH｜1.15 | |||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.2 | % | |
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜30 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 50%RH｜200 | % | |
| 洛氏硬度R | ASTM D-785 | DAM｜R121 | |||
| 洛氏硬度R | ASTM D-785 | 50%RH｜R109 | |||
| 洛氏硬度M | ASTM D-785 | DAM｜M87 | |||
| 洛氏硬度M | ASTM D-785 | 50%RH｜M80 | |||
| 剪切强度 | 23℃ | ASTM D-732 | DAM｜72.4 | MPa | |
| 剪切强度 | 23℃ | ASTM D-732 | 50%RH｜68.9 | MPa | |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜43 | j/m | |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 50%RH｜107 | j/m | |
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜2964 | MPa | |
| 揉曲模量 | 23℃ | ASTM D-790 | 50%RH｜1310 | MPa | |
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | ||
| 屈服伸长率 | ASTM D-638 | 50%RH｜25 | % | ||
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜90.3 | MPa | |
| 拉伸强度 | 23℃ | ASTM D-638 | 50%RH｜62.1 | MPa | |
| 屈服强度 | 23℃ | DAM｜90.3 | MPa | ||
| 屈服强度 | 23℃ | 50%RH｜62.1 | MPa | ||
| 介电常数 | 100Hz(cps) | ASTM D-150 | DAM｜4.0 | ||
| 介电常数 | 100Hz(cps) | ASTM D-150 | 50%RH｜8.0 | ||
| 耗散因数 | 103Hz(cps) | ASTM D-150 | DAM｜0.03 | ||
| 耗散因数 | 103Hz(cps) | ASTM D-150 | 50%RH｜0.12 | ||
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜3.9 | ||
| 介电常数 | 103Hz(cps) | ASTM D-150 | 50%RH｜7.0 | ||
| 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜3.6 | ||
| 介电常数 | 106Hz(cps) | ASTM D-150 | 50%RH｜4.6 | ||
| 体积电阻率 | ASTM D-257 | DAM｜1014 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 50%RH｜1012 | Ω.cm | ||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | 50%RH｜0.13 | ||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | DAM｜0.03 | ||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | 50%RH｜0.08 | ||
| UL可燃性导级 | UL 94 | DAM｜94 | |||
| UL可燃性导级 | UL 94 | 50%RH｜V-2 | |||
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜255 | ℃ | |
| 熔点 | Fisher Johns法 | ASTM D-789 | 50%RH｜255 | ℃ | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜90 | ℃ | |
| 热畸变温度 | 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜240 | ℃ | |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | 50%RH｜- | ℃ | |
| 脆化温度 | ASTM D-746 | DAM｜-52 | ℃ | ||
| 脆化温度 | ASTM D-746 | 50%RH｜-52 | ℃ | ||
| 需氧指数 | ASTM D-2863 | DAM｜25 | % | ||
| 需氧指数 | ASTM D-2863 | 50%RH｜31 | % | ||
| 关于美国杜邦 BK-10A价格 | |||||
| 1.有关“PA66 美国杜邦 BK-10A”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26263-0.htmlPA66 美国杜邦 BK-10A
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。