| 其它 其它 注塑 | |
| 适合超高抗冲击性的工程制品 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 24hr | ASTM D-570 | 1.2 | % | |
| 阻燃性 | UL 94 | DAM｜0.81 | mm | ||
| 阻燃性 | UL 94 | 50%RH｜- | mm | ||
| 比重 | ASTM D-792 | DAM｜1.09 | |||
| 比重 | ASTM D-792 | 50%RH｜- | |||
| 模具收缩率 | 3.2mm | DAM｜1.5 | % | ||
| 模具收缩率 | 3.2mm | 50%RH｜- | % | ||
| 阻燃性 | UL 94 | HB | |||
| 断裂伸长率 | ASTM D-638 | DAM｜80 | % | ||
| 断裂伸长率 | ASTM D-638 | 50%RH｜270 | % | ||
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | ||
| 屈服伸长率 | ASTM D-638 | 50%RH｜15 | % | ||
| IZOD冲击强度 | ASTM D-256 | DAM｜229 | J/m | ||
| IZOD冲击强度 | ASTM D-256 | 50%RH｜240 | J/m | ||
| 弯曲模量 | ASTM D-790 | DAM｜1965 | MPa | ||
| 弯曲模量 | ASTM D-790 | 50%RH｜1103 | MPa | ||
| 拉伸屈服强度 | ASTM D-638 | DAM｜60.7 | MPa | ||
| 拉伸屈服强度 | ASTM D-638 | 50%RH｜5.17 | MPa | ||
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜60.7 | MPa | |
| 拉伸强度 | 23℃ | ASTM D-638 | 50%RH｜51.7 | MPa | |
| 体积电阻率 | ASTM D-257 | DAM｜1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 50%RH｜1013 | Ω.cm | ||
| 热变形温度 | 0.45MPa | ASTM D-648 | DAM｜227 | ℃ | |
| 热变形温度 | 0.45MPa | ASTM D-648 | 50%RH｜- | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | DAM｜75 | ℃ | |
| 热变形温度 | 1.80MPa | ASTM D-648 | 50%RH｜- | ℃ | |
| 熔点 | ASTM D-3418 | DAM｜263 | ℃ | ||
| 熔点 | ASTM D-3418 | 50%RH｜- | ℃ | ||
| CLTE | ASTM D-696 | DAM｜0.81 | 10-4/K | ||
| CLTE | ASTM D-696 | 50%RH｜- | 10-4/K | ||
| 关于美国杜邦 408L价格 | |||||
| 1.有关“PA66 美国杜邦 408L”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||