| 高强度 其它 注塑 | |
| 特性：高强度33%玻纤 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 饱和(23℃) | ASTM D-570 | 5.4 | % | |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.7 | % | |
| 比重 | ASTM D-792 | 1.38 | |||
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % | |
| 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
| 拉伸强度 | 23℃,DAM | ASTM D-638 | 196.1 | MPa | |
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 6205 | MPa | |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 124.1 | MPa | |
| 洛氏硬度M | DAM | ASTM D-785 | M101 | ||
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 8963 | MPa | |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 86 | MPa | |
| 泰伯磨耗量 | 50%RH | 14 | cycles | ||
| 埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 107 | j/m | |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 133 | j/m | |
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 262 | MPa | |
| 介电强度 | (分步法)DAM | ASTM D-149 | 440 | volts/mil | |
| 介电常数 | 100% b9ebf1f98889>[email protected] | ASTM D-150 | 10.7 | ||
| 介电常数 | 100% 386a70780908>[email protected] | ASTM D-150 | 25.0 | ||
| 体积电阻率 | 100%RH | ASTM D-257 | 10 | ohm-cm | |
| 介电常数 | 85c1c4c8c5b4b5>[email protected] | ASTM D-150 | 3.7 | ||
| 介电强度 | DAM | ASTM D-149 | 530 | volts/mil | |
| 损耗因数 | a2e6e3efe29392>[email protected] | ASTM D-150 | 0.02 | ||
| 体积电阻率 | DAM | ASTM D-257 | 10 | ohm-cm | |
| 介电常数 | 4f0b0e020f7e7f>[email protected] | ASTM D-150 | 4.5 | ||
| 损耗因数 | 6622272b265756>[email protected] | ASTM D-150 | 0.02 | ||
| 热畸变温度 | 1.8MPa | ASTM D-648 | 249 | ℃ | |
| 熔点 | 50%RH | ASTM D-789 | 255 | ℃ | |
| 熔点 | ASTM D-789 | DAM | 255 | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | 2.3×10 | m/m/℃ | ||
| 关于美国杜邦 70G33HS1-L价格 | |||||
| 1.有关“PA66 美国杜邦 70G33HS1-L”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||