| 特性：尼龙-66基韧尼龙,低温下耐高冲。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜0.8 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 2.4%水｜- | % | |
| 比重 | ASTM D-792 | 无水｜1.07 | |||
| 比重 | ASTM D-792 | 2.4%水｜- | |||
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 无水｜20 | kgcm/cm | |
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 2.4%水｜- | kgcm/cm | |
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 无水｜95 | kgcm/cm | |
| IZOD冲击强度 | 23℃，V-缺口1/2 | ASTM D-256 | 2.4%水｜72 | kgcm/cm | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜50 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 2.4%水｜< 200 | % | |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 无水｜460 | Kg/cm2 | |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 2.4%水｜- | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜430 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 2.4%水｜360 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜16800 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 2.4%水｜8000 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜670 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 2.4%水｜360 | Kg/cm2 | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜65 | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 2.4%水｜- | ℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜203 | ℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 2.4%水｜- | ℃ | |
| 关于日本东丽 UTN325价格 | |||||
| 1.有关“PA66 日本东丽 UTN325”物性表及PA66塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26327-0.htmlPA66 日本东丽 UTN325
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。
上一篇：PA66 平顶山神马 2103T
下一篇：PA66 日本东丽 UTN320