| 其它 其它 注塑 | |
| 特性：玻纤45%强化，高模量。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜0.4 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 1.0%水｜- | % | |
| 比重 | ASTM D-792 | 无水｜1.5 | |||
| 比重 | ASTM D-792 | 1.0%水｜- | |||
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜138000 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 1.0%水｜128000 | Kg/cm2 | |
| IZOD冲击强度 | -40℃，无缺口1/8 | 无水｜85 | kgcm/cm2 | ||
| IZOD冲击强度 | -40℃，无缺口1/8 | 1.0%水｜93 | kgcm/cm2 | ||
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 无水｜9.5 | kgcm/cm | |
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 1.0%水｜10 | kgcm/cm | |
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜90 | kgcm/cm2 | ||
| IZOD冲击强度 | 23℃，无缺口1/8 | 1.0%水｜100 | kgcm/cm2 | ||
| IZOD冲击强度 | 23℃，V缺口1/2 | ASTM D-256 | 无水｜10 | kgcm/cm | |
| IZOD冲击强度 | 23℃，V缺口1/2 | ASTM D-256 | 1.0%水｜14 | kgcm/cm | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜2150 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 1.0%水｜1700 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜3400 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 1.0%水｜3150 | Kg/cm2 | |
| 压缩强度 | -40℃ | ASTM D-695 | 无水｜2700 | Kg/cm2 | |
| 压缩强度 | -40℃ | ASTM D-695 | 1.0%水｜- | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜2150 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 1.0%水｜1700 | Kg/cm2 | |
| 断裂伸长率 | -40℃ | ASTM D-648 | 无水｜4.5 | % | |
| 断裂伸长率 | -40℃ | ASTM D-648 | 1.0%水｜- | % | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜103 | M-标度 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1.0%水｜- | M-标度 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜3000 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1.0%水｜2500 | Kg/cm2 | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 无水｜9 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 1.0%水｜- | % | |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜2000 | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 1.0%水｜- | Kg/cm2 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 1.0%水｜5 | % | |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜1050 | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 1.0%水｜- | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜2800 | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 1.0%水｜2650 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜1950 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 1.0%水｜1650 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜125000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 1.0%水｜98000 | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜121 | R-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 1.0%水｜- | R-标度 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜81000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 1.0%水｜65000 | Kg/cm2 | |
| 压缩强度 | 80℃ | ASTM D-695 | 无水｜1200 | Kg/cm2 | |
| 压缩强度 | 80℃ | ASTM D-695 | 1.0%水｜- | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜2150 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 1.0%水｜1700 | Kg/cm2 | |
| 体积电阻率 | ASTM D-257 | 无水｜1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 1.0%水｜1012-1013 | Ω.cm | ||
| 介电强度 | 1/8 | ASTM D-149 | 无水｜19 | KV/mm | |
| 介电强度 | 1/8 | ASTM D-149 | 1.0%水｜- | KV/mm | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜263 | ℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 1.0%水｜- | ℃ | |
| 线性热膨胀系数 | ASTM D-696 | 无水｜2-3 | ×10-5cm/cm/℃ | ||
| 关于日本东丽 CM3001G-45价格 | |||||
| 1.有关“PA66 日本东丽 CM3001G-45”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||