| 其它 其它 注塑 | |
| 类型：尼龙-66未强化 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜1.2 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 2.5%水｜- | % | |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 无水｜8 | mg/1000次 | |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 2.5%水｜- | mg/1000次 | |
| 比重 | ASTM D-792 | 无水｜1.13-1.14 | |||
| 比重 | ASTM D-792 | 2.5%水｜- | |||
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜790 | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 2.5%水｜770 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜29000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 2.5%水｜14000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜9000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 2.5%水｜5000 | Kg/cm2 | |
| IZOD冲击强度 | -40℃，V缺口1/2 | 无水｜3.5 | kg.cm/cm | ||
| IZOD冲击强度 | -40℃，V缺口1/2 | 2.5%水｜- | kg.cm/cm | ||
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1150 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 2.5%水｜650 | Kg/cm2 | |
| 抗拉断裂强度 | 230℃ | ASTM D-638 | 无水｜700 | Kg/cm2 | |
| 抗拉断裂强度 | 230℃ | ASTM D-638 | 2.5%水｜730 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜1450 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 2.5%水｜1300 | Kg/cm2 | |
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜无断裂 | kg.cm/cm | ||
| IZOD冲击强度 | 23℃，无缺口1/8 | 2.5%水｜- | kg.cm/cm | ||
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜430 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 2.5%水｜400 | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜1150 | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 2.5%水｜1100 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜44000 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 2.5%水｜42000 | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜97 | R | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 2.5%水｜- | R | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜800 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 2.5%水｜530 | Kg/cm2 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜110 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 2.5%水｜< 200 | % | |
| IZOD冲击强度 | 23℃，V缺口1/2 | 无水｜5 | kg.cm/cm | ||
| IZOD冲击强度 | 23℃，V缺口1/2 | 2.5%水｜28 | kg.cm/cm | ||
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜640 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 2.5%水｜400 | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜910 | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 2.5%水｜- | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜119 | R | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 2.5%水｜100 | R | |
| 介电常数 | 50HZ | ASTM D-150 | 无水｜4 | ||
| 介电常数 | 50HZ | ASTM D-150 | 2.5%水｜- | ||
| 抗电弧性 | 1/8 | ASTM D-150 | 无水｜128 | ||
| 抗电弧性 | 1/8 | ASTM D-150 | 2.5%水｜- | ||
| 损耗因素 | 103Hz | ASTM D-150 | 无水｜0.03 | ||
| 损耗因素 | 103Hz | ASTM D-150 | 2.5%水｜- | ||
| 介电强度 | 1/8 | ASTM D-149 | 无水｜18 | KV/mm | |
| 介电强度 | 1/8 | ASTM D-149 | 2.5%水｜- | KV/mm | |
| 介电常数 | 103Hz | ASTM D-150 | 无水｜3.9 | ||
| 介电常数 | 103Hz | ASTM D-150 | 2.5%水｜- | ||
| 体积电阻率 | ASTM D-257 | 无水｜1014-1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 2.5%水｜1011-1012 | Ω.cm | ||
| 介电常数 | 106Hz | ASTM D-150 | 无水｜3.3 | ||
| 介电常数 | 106Hz | ASTM D-150 | 2.5%水｜3.8 | ||
| 损耗因素 | 106Hz | ASTM D-150 | 无水｜0.02 | ||
| 关于日本东丽 CM3001-N价格 | |||||
| 1.有关“PA66 日本东丽 CM3001-N”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26341-0.htmlPA66 日本东丽 CM3001-N
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。
上一篇：PA66 日本东丽 CM3003
下一篇：PA66 日本旭化成 FG173