| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 密度 | ISO1183 | 1.13 | g/cm3 | ||
| 吸水率(24hr) | ASTMD570 | 1.6 | % | ||
| 吸水率(23°C,24hr) | ISO62 | 1.6 | % | ||
| 吸水率(饱和) | ASTMD570 | 9.2 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 9.2 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 2.6 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 2.6 | % | ||
| 抗张强度 | 屈服,-40°C | ASTMD638 | 138 | MPa | |
| 抗张强度 | 屈服,23°C | ASTMD638 | 84.0 | MPa | |
| 抗张强度 | Yield,121°C | ASTMD638 | 24.0 | MPa | |
| 拉伸应力(屈服,23°C) | ISO527-2 | 77.0 | MPa | ||
| 伸长率(屈服,23°C) | ASTMD638 | 4.0 | % | ||
| 拉伸应变(屈服,23°C) | ISO527-2 | 4.0 | % | ||
| 伸长率(断裂,23°C) | ASTMD638 | >100 | % | ||
| 弯曲模量 | -40°C | ASTMD790 | 3160 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 2900 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 435 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 310 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 260 | MPa | |
| 弯曲模量(23°C) | ISO178 | 2900 | MPa | ||
| 弯曲强度 | -40°C | ASTMD790 | 179 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 114 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 30.0 | MPa | |
| 弯曲强度 | 90°C | ASTMD790 | 20.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 17.0 | MPa | |
| 弯曲应力(23°C) | ISO178 | 114 | MPa | ||
| 简支梁缺口冲击强度(23°C) | ISO179 | 6.4 | kJ/m2 | ||
| 简支梁无缺口冲击强度(23°C) | ISO179 | 390 | kJ/m2 | ||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 53 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 53 | J/m | |
| 洛氏硬度(R级) | ASTMD785 | 99 | |||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 169 | °C | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/B | 169 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 63.0 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 63.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 溶融温度（DSC） | ISO3146 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 1.4E-4 | cm/cm/°C | ||
| RTIElec | 0.75mm | UL746 | 65.0 | °C | |
| RTIElec | 6.0mm | UL746 | 65.0 | °C | |
| RTIImp | 0.75mm | UL746 | 65.0 | °C | |
| RTIImp | 6.0mm | UL746 | 65.0 | °C | |
| RTIStr | 0.75mm | UL746 | 65.0 | °C | |
| RTIStr | 6.0mm | UL746 | 65.0 | °C | |
| UL阻燃等级 | 0.75mm | UL94 | HB | ||
| UL阻燃等级 | 6.0mm | UL94 | V-2 | ||
| 补充信息 | TestMethod | Dry | Unit | ||
| BlowMoldingDryingTemperature | 80 | °C | |||
| BlowMoldingDryingTime | 2.0to4.0 | hr | |||
| BlowMoldingMeltTemperature | 245to260 | °C | |||
| BlowMoldingMoistureContent | <0.15 | % | |||
| BlowMoldingMoldTemperature | 60 | °C | |||
| Blow-upRatio | 2:1 | ||||
| 关于德国巴斯夫 Ultramid® 8270 HS价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8270 HS”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-21969-0.htmlPA6 德国巴斯夫 Ultramid® 8270 HS