| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 1.2 | % | |||
| 吸水率(24hr) | ASTMD570 | 1.6 | % | ||
| 吸水率(饱和) | ASTMD570 | 9.5 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 2.7 | % | ||
| 抗张强度 | 屈服,-40°C | ASTMD638 | 125 | MPa | |
| 抗张强度 | 屈服,23°C | ASTMD638 | 79.0 | MPa | |
| 抗张强度 | 屈服,80°C | ASTMD638 | 35.0 | MPa | |
| 抗张强度 | Yield,121°C | ASTMD638 | 25.0 | MPa | |
| 抗张强度(断裂,23°C) | ASTMD638 | 75.0 | MPa | ||
| 伸长率 | 屈服,23°C | ASTMD638 | 4.0 | % | |
| 伸长率 | 屈服,80°C | ASTMD638 | 42 | % | |
| 伸长率 | Yield,121°C | ASTMD638 | 36 | % | |
| 伸长率(断裂,23°C) | ASTMD638 | 55 | % | ||
| 弯曲模量 | -40°C | ASTMD790 | 3010 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 2830 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 500 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 350 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 305 | MPa | |
| 弯曲强度 | -40°C | ASTMD790 | 170 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 110 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 30.0 | MPa | |
| 弯曲强度 | 90°C | ASTMD790 | 20.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 20.0 | MPa | |
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 50 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 60 | J/m | |
| 洛氏硬度(R级) | ASTMD785 | 119 | |||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 178 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 65.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 8.3E-5 | cm/cm/°C | ||
| 关于德国巴斯夫 Ultramid® 8202 L价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8202 L”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||