| 高强度,清晰度，高,良好的开裂抵抗 | |
| 包装,双向拉伸薄膜 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 摩擦系数 | 与金属-动态 | ASTMD1894 | 0.17 | ||
| 摩擦系数 | 与自身-动态 | ASTMD1894 | 0.44 | ||
| 薄膜厚度-经测试 | 8.1 | um | |||
| 割线模量 | MD:8.1um | ASTMD882 | 2760 | MPa | |
| 割线模量 | TD:8.1um | ASTMD882 | 1900 | MPa | |
| 抗张强度 | MD:断裂,8.1um | ASTMD882 | 241 | MPa | |
| 抗张强度 | TD:断裂,8.1um | ASTMD882 | 290 | MPa | |
| 伸长率 | MD:断裂,8.1um | ASTMD882 | 90 | % | |
| 伸长率 | TD:断裂,8.1um | ASTMD882 | 75 | % | |
| 透氧率(25°C,8.1um) | ASTMD3985 | 2.1 | cm3mm/m2/atm/24hr | ||
| 水气透过率(8.0um,38°C,100%RH) | ASTMF1249 | 530 | gmm/m2/atm/24hr | ||
| 薄膜厚度-经测试 | 8.1 | um | |||
| 割线模量 | MD:8.1um | ASTMD882 | 2760 | MPa | |
| 割线模量 | TD:8.1um | ASTMD882 | 1900 | MPa | |
| 抗张强度 | MD:断裂,8.1um | ASTMD882 | 241 | MPa | |
| 抗张强度 | TD:断裂,8.1um | ASTMD882 | 290 | MPa | |
| 伸长率 | MD:断裂,8.1um | ASTMD882 | 90 | % | |
| 伸长率 | TD:断裂,8.1um | ASTMD882 | 75 | % | |
| 透氧率(25°C,8.1um) | ASTMD3985 | 2.1 | cm3mm/m2/atm/24hr | ||
| 水气透过率(8.0um,38°C,100%RH) | ASTMF1249 | 530 | gmm/m2/atm/24hr | ||
| 光泽度(20°,8.13um) | ASTMD2457 | 150 | |||
| 雾度(8.13um) | ASTMD1003 | 2.5 | % | ||
| 关于美国Honeywell Capran Medallion® 800价格 | |||||
| 1.有关“PA6 美国Honeywell Capran Medallion® 800”物性表及PA6塑料颗粒价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168 | |||||
本文链接：http://www.28at.com/showinfo-41-25056-0.htmlPA6 美国Honeywell Capran Medallion® 800
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。