| 阻燃 其它 其它 | |
| 特性：玻纤增强30%,阻燃等级，含卤素。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜0.4 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 1.3%水｜- | % | |
| 比重 | ASTM D-792 | 无水｜1.59 | |||
| 比重 | ASTM D-792 | 1.3%水｜- | |||
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜65 | kg.cm/cm | ||
| IZOD冲击强度 | 23℃，无缺口1/8 | 1.3%水｜70 | kg.cm/cm | ||
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 无水｜1640 | Kg/cm2 | |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 1.3%水｜1350 | Kg/cm2 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 1.3%水｜5 | % | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜2490 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1.3%水｜2000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜93200 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 1.3%水｜65000 | Kg/cm2 | |
| 体积电阻率 | ASTM D-257 | 无水｜8×1014 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 1.3%水｜8×1013 | Ω.cm | ||
| 介电强度 | 1/8 | ASTM D-149 | 无水｜38 | KV/mm | |
| 介电强度 | 1/8 | ASTM D-149 | 1.3%水｜33 | KV/mm | |
| IEC导电径迹指数 | UL 746 | 无水｜200 | V | ||
| IEC导电径迹指数 | UL 746 | 1.3%水｜- | V | ||
| 损耗因数 | 106Hz | ASTM D-150 | 无水｜0.003-0.009 | ||
| 损耗因数 | 106Hz | ASTM D-150 | 1.3%水｜- | ||
| 抗电弧性 | 1/8 | ASTM D-495 | 无水｜70-80 | s | |
| 抗电弧性 | 1/8 | ASTM D-495 | 1.3%水｜- | s | |
| 线性热膨胀系数 | ASTM D-696 | 无水｜2 | 10-5cm/cm.℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 1.3%水｜- | |||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜251 | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- | ℃ | |
| 熔点 | 差示扫描测热计DSC法 | 无水｜265 | ℃ | ||
| 熔点 | 差示扫描测热计DSC法 | 1.3%水｜- | ℃ | ||
| UL-94抗燃级 | UL 94 | 无水｜V-0 | |||
| UL-94抗燃级 | UL 94 | 1.3%水｜- | |||
| 强化含量 | 无水｜30 | WT% | |||
| 强化含量 | 1.3%水｜- | WT% | |||
| 关于日本东丽 CM3004G-30价格 | |||||
| 1.有关“PA66 日本东丽 CM3004G-30”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26332-0.htmlPA66 日本东丽 CM3004G-30
声明：本网页内容旨在传播知识，不代表本站观点，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。
上一篇：PA66 日本东丽 CM3006