| 其它 其它 注塑 | |
| 类型：尼龙-66未强化 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜1.2 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 3.5%水｜- | % | |
| 比重 | ASTM D-792 | 无水｜1.13-1.14 | |||
| 比重 | ASTM D-792 | 3.5%水｜- | |||
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 无水｜8 | mg/1000次 | |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- | mg/1000次 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜90 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 3.5%水｜< 200 | % | |
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 无水｜3.5 | kgcm/cm | |
| IZOD冲击强度 | -40℃，V缺口1/2 | ASTM D-256 | 3.5%水｜- | kgcm/cm | |
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜44000 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 3.5%水｜42000 | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜97 | M-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 3.5%水｜- | M-标度 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜790 | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 3.5%水｜770 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜640 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 3.5%水｜400 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜9000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 3.5%水｜5000 | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜119 | R-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 3.5%水｜100 | R-标度 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜29000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 3.5%水｜14000 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜800 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 3.5%水｜530 | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜910 | Kg/cm2 | |
| 压缩强度 | 23℃ | ASTM D-695 | 3.5%水｜- | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1150 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 3.5%水｜650 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜430 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 3.5%水｜400 | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜1150 | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 3.5%水｜1100 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜1450 | Kg/cm2 | |
| 挠曲强度 | -40℃ | ASTM D-790 | 3.5%水｜1300 | Kg/cm2 | |
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜无断裂 | kgcm/cm2 | ||
| IZOD冲击强度 | 23℃，无缺口1/8 | 3.5%水｜- | kgcm/cm2 | ||
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜800 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 3.5%水｜530 | Kg/cm2 | |
| IZOD冲击强度 | 23℃，V缺口1/2 | ASTM D-256 | 无水｜5 | kgcm/cm | |
| IZOD冲击强度 | 23℃，V缺口1/2 | ASTM D-256 | 3.5%水｜28 | kgcm/cm | |
| IEC导电径迹指数 | UL 746 | 无水｜- | V | ||
| IEC导电径迹指数 | UL 746 | 3.5%水｜530 | V | ||
| 介电常数 | 50Hz | ASTM D-150 | 无水｜1.6 | ||
| 介电常数 | 50Hz | ASTM D-150 | 3.5%水｜- | ||
| 体积电阻率 | ASTM D-257 | 无水｜1014-1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 3.5%水｜1012-1013 | Ω.cm | ||
| 损耗因数 | 50Hz | ASTM D-150 | 无水｜0.06 | ||
| 损耗因数 | 50Hz | ASTM D-150 | 3.5%水｜- | ||
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 无水｜220 | ℃ | |
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 | 3.5%水｜- | ℃ | |
| 熔点 | 差示扫描测热计DSC | 无水｜265 | ℃ | ||
| 熔点 | 差示扫描测热计DSC | 3.5%水｜- | ℃ | ||
| 比热 | 无水｜0.4 | Cal/g℃ | |||
| 比热 | 3.5%水｜- | Cal/g℃ | |||
| 线性热膨胀系数 | ASTM D-696 | 无水｜9-10 | ×10-5cm/cm/℃ | ||
| 关于日本东丽 CM3006价格 | |||||
| 1.有关“PA66 日本东丽 CM3006”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||