| 其它 其它 注塑 | |
| 特性：玻纤15%K强化，阻燃剂。 | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜0.5 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 1.3%水｜- | % | |
| 比重 | ASTM D-792 | 无水｜1.47 | |||
| 比重 | ASTM D-792 | 1.3%水｜- | |||
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜40 | kg.cm/cm | ||
| IZOD冲击强度 | 23℃，无缺口1/8 | 1.3%水｜48 | kg.cm/cm | ||
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 无水｜1240 | Kg/cm2 | |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 1.3%水｜950 | Kg/cm2 | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜5 | % | |
| 断裂伸长率 | 23℃ | ASTM D-638 | 1.3%水｜5 | % | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1880 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1.3%水｜1400 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜57100 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 1.3%水｜35000 | Kg/cm2 | |
| 体积电阻率 | ASTM D-257 | 无水｜8×1014 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 1.3%水｜8×1012 | Ω.cm | ||
| 介电强度 | 1/8 | ASTM D-149 | 无水｜31 | KV/mm | |
| 介电强度 | 1/8 | ASTM D-149 | 1.3%水｜26 | KV/mm | |
| IEC导电径迹指数 | UL 746 | 无水｜210 | V | ||
| IEC导电径迹指数 | UL 746 | 1.3%水｜- | V | ||
| 介电常数 | 106Hz | ASTM D-150 | 无水｜4 | ||
| 介电常数 | 106Hz | ASTM D-150 | 1.3%水｜- | ||
| 损耗因数 | 106Hz | ASTM D-150 | 无水｜0.003-0.01 | ||
| 损耗因数 | 106Hz | ASTM D-150 | 1.3%水｜- | ||
| 抗电弧性 | 1/8 | ASTM D-495 | 无水｜70 | s | |
| 抗电弧性 | 1/8 | ASTM D-495 | 1.3%水｜- | s | |
| 线性热膨胀系数 | ASTM D-696 | 无水｜5 | 10-5cm/cm.℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 1.3%水｜- | |||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜244 | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- | ℃ | |
| 熔点 | 差示扫描测热计DSC法 | 无水｜265 | ℃ | ||
| 熔点 | 差示扫描测热计DSC法 | 1.3%水｜- | ℃ | ||
| UL-94抗燃级 | UL 94 | 无水｜V-0 | |||
| UL-94抗燃级 | UL 94 | 1.3%水｜- | |||
| 强化含量 | 无水｜15 | WT% | |||
| 强化含量 | 1.3%水｜- | WT% | |||
| 关于日本东丽 CM3004G-15价格 | |||||
| 1.有关“PA66 日本东丽 CM3004G-15”物性表及PA66塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系. | |||||